谢建丽,卢叶艇,吴立新.核电厂冷冻水系统更换缓蚀剂的可行性评估[J].表面技术,2015,44(7):114-119.
XIE Jian-li,LU Ye-ting,WU Li-xin.Feasibility of Replacing Inhibitor for Chilled Water System of Nuclear Power Plant[J].Surface Technology,2015,44(7):114-119
核电厂冷冻水系统更换缓蚀剂的可行性评估
Feasibility of Replacing Inhibitor for Chilled Water System of Nuclear Power Plant
投稿时间:2015-02-13  修订日期:2015-07-20
DOI:10.16490/j.cnki.issn.1001-3660.2015.07.021
中文关键词:  核电厂  冷冻水系统  缓蚀剂  LiOH-联氨处理  防腐
英文关键词:nuclear power plant  chilled water system  inhibitor  LiOH-N2 H4 treatment  anti-corrosion
基金项目:
作者单位
谢建丽 苏州热工研究院有限公司, 江苏 苏州 215004 
卢叶艇 中核核电运行管理有限公司, 浙江 海盐 314303 
吴立新 中核核电运行管理有限公司, 浙江 海盐 314303 
AuthorInstitution
XIE Jian-li Suzhou Nuclear Power Research Institute, Suzhou 215004, China 
LU Ye-ting China National Nuclear Corporation, Haiyan 314303, China 
WU Li-xin China National Nuclear Corporation, Haiyan 314303, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 评估缓蚀剂更换过程对核电厂冷冻水系统管材防腐的影响。 方法 采用线性极化、交流阻抗、强极化等电化学方法以及扫描电镜、X 射线衍射等表面分析技术,研究在从原缓蚀剂(NaNO2-Na2MoO4 介质)向新缓蚀剂(LiOH-联氨介质)置换过程中,A106B 碳钢及 B10 铜镍合金等两种主体管材的耐蚀性能变化。 结果 电化学测量表明,缓蚀剂置换过程中,两种管材的极化电阻 Rp 和传递电阻 Rt 总体上逐渐增大,腐蚀电流 Jcorr逐渐减小。 表面分析表明,金属在原缓蚀剂中表面较光滑,换水过程中逐渐生成锈层,在新缓蚀剂中锈层未见明显发展。 结论 原 NaNO2-Na2MoO4 介质可抑制金属阳极腐蚀过程,对金属材质有良好的保护效果。 换水阶段,A106B 碳钢发生均匀腐蚀,表面积聚有锈层;B10 铜镍合金腐蚀程度较轻微,两种材质的耐蚀性能均未见明显降低。 新 LiOH-联氨介质可继续对带锈层金属起保护作用,可增强锈层致密性,使金属材质的耐蚀性进一步提高。 以 LiOH-联氨介质置换 NaNO2-Na2MoO4介质,作为核电厂冷冻水的缓蚀剂具有可行性及可操作性。
英文摘要:
      Objective To assess the influence of replacing inhibitors on the anti-corrosion treatment of chilled water system. Methods This paper studied the changes of corrosion resistance of A106B and B10 in the replacement process from the original in-hibitor (NaNO2-Na2MoO4) to a new inhibitor (LiOH-N2H4) by the means of electrochemical tests and surface analysis methods, such as linear polarization and AC impedance tests, SEM and XRD. Results The electrochemical results showed that the Rp value and Rt value of two pipe materials increased gradually while the Icorr value decreased in the replacement process of inhibitors. The surface analysis results showed that there was little rust on metal surfaces in original inhibitor solution, the rust layers were formed during the replacement process of inhibitors, and the rust layers were not thickened in the new inhibitor solution. Conclusion The original NaNO2-Na2MoO4 medium had a good protective effect on the metal above by inhibiting anodic corrosion process. A106B carbon steel suffered a uniform corrosion and a rust layer formed on its surface, while B10 copper-nickel ally had a lesser degree of corrosion when the inhibitor was replacing, indicating the anti-corrosion property of the two materials was not decreased. The novel LiOH-N2 H4 medium, which can enhance the compactness of rust, was able to reduce the corrosion rate of rusted metal and increase the corrosion resistance of metals. It is feasible and operable to replace NaNO2 -Na2 MoO4 with LiOH-N2 H4 medium for the anti-cor-rosion treatment of chilled water system of nuclear power plant.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第13594465位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: wjqkbm@163.com

渝公网安备 50010702501715号