朱理奎,周小平,方锳泽.Ni-Cr-Al 涂层搅拌摩擦加工的作用机制[J].表面技术,2015,44(6):59-64,87.
ZHU Li-kui,ZHOU Xiao-ping,FANG Ying-ze.Friction Stir Processing Mechanism of Ni-Cr-Al Coating Layer[J].Surface Technology,2015,44(6):59-64,87
Ni-Cr-Al 涂层搅拌摩擦加工的作用机制
Friction Stir Processing Mechanism of Ni-Cr-Al Coating Layer
投稿时间:2015-01-07  修订日期:2015-06-20
DOI:10.16490/j.cnki.issn.1001-3660.2015.06.012
中文关键词:  细晶化  塑性变形  元素互扩散  显微硬度
英文关键词:fine crystallization  plastic deformation  element interdiffusion  microhardness
基金项目:国家自然科学基金资助(51171062)
作者单位
朱理奎 1. 湖北工业大学 机械工程学院, 武汉 430068; 2. 绿色轻工材料湖北省重点实验室, 武汉 430068 
周小平 1. 湖北工业大学 机械工程学院, 武汉 430068; 2. 绿色轻工材料湖北省重点实验室, 武汉 430068 
方锳泽 1. 湖北工业大学 机械工程学院, 武汉 430068; 2. 绿色轻工材料湖北省重点实验室, 武汉 430068 
AuthorInstitution
ZHU Li-kui 1. School of Mechanical Engineering, Hubei University of Technology, Wuhan 430068, China;2. Hubei Provincial Key Laboratory of Green Materials for Light Industry, Wuhan 430068, China 
ZHOU Xiao-ping 1. School of Mechanical Engineering, Hubei University of Technology, Wuhan 430068, China;2. Hubei Provincial Key Laboratory of Green Materials for Light Industry, Wuhan 430068, China 
FANG Ying-ze 1. School of Mechanical Engineering, Hubei University of Technology, Wuhan 430068, China;2. Hubei Provincial Key Laboratory of Green Materials for Light Industry, Wuhan 430068, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 对热喷涂涂层进行表面改性。 方法 利用搅拌摩擦加工技术多道次加工制备复合层,分析受影响区涂层和基体的显微组织、元素扩散、显微硬度变化规律。 结果 形成了均匀致密且细晶化、涂层与界面消失、靠近涂层部分基体发生动态再结晶的复合层。 从涂层到基体形成了有层次的 260 μm 厚度渐变影响区,依次为:BZ,RLS,FRZ,ECZ。 温度场和塑性变形的耦合作用为涂层和基体元素互扩散提供了有利通道,发生了快速元素互扩散。 细晶强化和元素扩散共同作用使显微硬度显著提高,机械性能得到改善。 结论 搅拌摩擦加工技术能有效改善热喷涂涂层的组织和性能。
英文摘要:
      Objective To improve the thermal spraying coating layer. Methods Composite layer was prepared by using multipass friction stir processing technology. The transformation regulation of microscopic structure, element diffusion and microhardness were analyzed both on the affected area coating layer and substrate. Results A composite layer of uniform density and fine crystallization, interface of coating layer and substrate disappeared, dynamic recrystallization occurred was formed. A 260 μm hierarchical gradient affected zone was formed from the coating layer to the substrate: BZ, RLS, FRZ, ECZ. The coupling effect of temperature and plastic deformation provided favorable channel to fast element interdiffusion. Combination of fine-grain and elements diffusion obviously improved the microhardness and mechanical performance. Conclusion Friction stir processing technology can effectively improve the microscopic structure and properties of thermal spray coating layer.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19885652位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号