罗傲梅,郭伟.纵-扭复合振动超声深滚加工表面强化研究[J].表面技术,2015,44(5):106-110.
LUO Ao-mei,GUO Wei.Research on Surface Strengthening by Ultrasonic Deep Rolling with Longitudinal-Torsional Vibration[J].Surface Technology,2015,44(5):106-110
纵-扭复合振动超声深滚加工表面强化研究
Research on Surface Strengthening by Ultrasonic Deep Rolling with Longitudinal-Torsional Vibration
投稿时间:2015-01-08  修订日期:2015-05-20
DOI:10.16490/j.cnki.issn.1001-3660.2015.05.020
中文关键词:  超声深滚  纵-扭复合振动  表面强化  显微硬度
英文关键词:ultrasonic deep rolling  longitudinal-torsional vibration  surface strengthening  micro-hardness
基金项目:
作者单位
罗傲梅 河南工业和信息化职业学院 机械工程系, 河南 焦作 454003 
郭伟 河南工业和信息化职业学院 机械工程系, 河南 焦作 454003 
AuthorInstitution
LUO Ao-mei Department of Mechanical Engineering, Henan College of Industry & Information Technology, Jiaozuo 454003, China 
GUO Wei Department of Mechanical Engineering, Henan College of Industry & Information Technology, Jiaozuo 454003, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 基于纵-扭复合振动超声加工和超声深滚加工提出了纵-扭复合振动超声深滚加工工艺,研究各深滚工艺参数对工件表面强度的影响,以验证二维超声振动加工技术在表面强化技术领域的应用效果。 方法 采用单因素试验法对 6061-T651 铝合金轴件分别进行纵-扭复合振动超声深滚与常规深滚加工试验,然后用 MH-5 数显硬度计测试每组参数下的表面显微硬度,研究静压力、工件转速和进给量对工件表面显微硬度的影响,并将两种试验结果进行对比。 结果 在设定工艺参数内,纵-扭复合振动超声深滚工艺所获得的表面显微硬度均高于同等加工条件下常规深滚工艺。 纵-扭复合振动超声深滚加工时,表面显微硬度随静压力和工件转速的增大先增大后减小,随进给量的增大先减小后增大再减小;常规深滚加工时,表面显微硬度与静压力近似呈线性关系,且随工件转速的增大先增大后减小,随进给量的增大一直减小。 结论 纵-扭复合振动超声深滚加工工艺能更有效地实现 6061-T651 铝合金的表面强化处理。
英文摘要:
      Objective To propose ultrasonic deep rolling with longitudinal-torsional vibration (UDR-LTV) based on ultrasonic machining with longitudinal-torsional vibration and ultrasonic deep rolling, and to study the effects of processing parameters on surface strengthening, so as to verify the application effect of the two-dimensional ultrasonic vibration machining technology in the field of surface strengthening technology. Methods Conventional deep rolling (CDR) and UDR-LTV were applied using the single factor experiment to process aluminum alloy 6061-T651 respectively, then the surface micro-hardness was tested by each set of parameters with the MH-5 digital hardness tester to investigate the influence of static pressure, rotate-speed and feed amount on the surface micro-hardness. The results of the two processing ways in the experiment were compared. Results Within the set parameters, the surface micro-hardness obtained by UDR-LTV was larger than that of CDR under the same processing conditions. The surface microhardness increased at first then decreased with the increase of static pressure and rotate-speed, and decreased at first then increased and decreased at last with the increase of feed amount by UDR-LTV. The surface micro-hardness and static pressure showed an approximate linear relationship, and the surface micro-hardness increased at first then decreased with the increase of rotate-speed, and reduced all along with the increase of feed amount by CDR. Conclusion It is proved that aluminum alloy 6061-T651 may be more effectively strengthened when treated by UDR-LTV.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第13593393位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: wjqkbm@163.com

渝公网安备 50010702501715号