谢治辉.环保型 AZ91D 镁合金直接化学镀镍工艺研究[J].表面技术,2015,44(2):24-28,47.
XIE Zhi-hui.An Environmentally-friendly Process of Direct Electroless Nickel Plating on AZ91D Magnesium Alloy[J].Surface Technology,2015,44(2):24-28,47
环保型 AZ91D 镁合金直接化学镀镍工艺研究
An Environmentally-friendly Process of Direct Electroless Nickel Plating on AZ91D Magnesium Alloy
投稿时间:2014-10-06  修订日期:2015-02-20
DOI:10.16490/j.cnki.issn.1001-3660.2015.02.005
中文关键词:  镁合金  化学镀  前处理  稳定性
英文关键词:magnesium alloy  electroless plating  pretreatment  stability
基金项目:四川省教育厅自然科学基金项目(14ZB0147);化学合成与污染控制四川省重点实验室项目(CSPC-2014-4-2);西华师范大学基本科研业务费专项(13E006)
作者单位
谢治辉 西华师范大学 化学合成与污染控制四川省重点实验室, 四川 南充 637002 
AuthorInstitution
XIE Zhi-hui Chemical Synthesis and Pollution Control Key Laboratory of Sichuan Province,China West Normal University, Nanchong 637002, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 开发一种无铬、低氟、稳定的镁合金直接化学镀镍工艺。 方法 通过 SEM,EDX 及浸泡实验、动电位极化曲线、划格试验等方法,以稳定系数和镀速等参数为对象,对比新工艺和传统工艺对镀层或镀液性能的影响。 结果 在以硫酸镍为主盐的基础液中,添加质量浓度为 0. 5 mg/ L 的硫脲,镀液的稳定性可得到明显的提高。 在使用硝酸+磷酸酸洗后的镁合金试样表面,获得了良好的腐蚀形貌结构,这种结构有利于增强镀层与基底间的机械咬合作用。 新工艺获得的镀层属高 P 镀层(P 的质量分数约为11% ),在 NaCl 溶液中的自腐蚀电位由-1. 5 V 正℃至-0. 5 V,腐蚀电流密度降低了约 3 个数量级。 结论以硫酸镍主盐镀液获得的镀层耐蚀性优于碱式碳酸镍主盐镀液获得的镀层,镀液的最佳 pH=5,化学镀镍温度为 82 ℃。
英文摘要:
      Objective To develop a chromium-free and stable direct electroless nickel plating (ENP) technology for magnesium alloy. Methods SEM, EDX, immersion test, polarization curves, scribe and grid test as well as the stability factor and deposition rate were used to compare the effects of the new and traditional processes on the characteristics of the performance of Ni-P coating and plating bath. Results The stability of the base solution with nickel sulfate as the main salt could be obviously improved when 0. 5 mg/ L of thiourea was added. A good corrosion morphology structure of the AZ91D magnesium alloy was achieved after pickling in a mixture of nitric acid and phosphoric acid. This specific surface structure could improve the mechanical adhesion between the substrate and the coating. The coating prepared using the new technology belonged to high-P coating, with a P content of about 11% . Compared to the bare magnesium alloy, the potentiodynamic polarization test in NaCl solution showed that the corrosion potential and the corrosion current density of the new coating increased positively from -1. 5 V to -0. 5 V and decreased by three orders of magnitude, respectively. Conclusion The corrosion resistance of coating obtained from a plating bath using nickel sulfate as the main salt was better than that from a plating bath using basic nickel carbonate as the main salt. The optimal pH and temperature of the ENP processes were 5 and 82 ℃ , respectively.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19515045位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号