王双红,赵时璐.无取向硅钢环保绝缘涂层的制备与性能[J].表面技术,2015,44(1):117-121.
WANG Shuang-hong,ZHAO Shi-lu.Preparation and Performance of Insulating Coating on Non-oriented Silicon Steel[J].Surface Technology,2015,44(1):117-121
无取向硅钢环保绝缘涂层的制备与性能
Preparation and Performance of Insulating Coating on Non-oriented Silicon Steel
投稿时间:2014-08-10  修订日期:2015-01-20
DOI:
中文关键词:  无铬涂料  绝缘涂层  环保  磷酸盐  无取向硅钢
英文关键词:chromium-free coating  insulating coating  environment-friendly  phosphate  non-oriented silicon steel
基金项目:
作者单位
王双红 沈阳大学 机械工程学院, 沈阳 110044 
赵时璐 沈阳大学 机械工程学院, 沈阳 110044 
AuthorInstitution
WANG Shuang-hong College of Mechanical Engineering, Shenyang University, Shenyang 110044, China 
ZHAO Shi-lu College of Mechanical Engineering, Shenyang University, Shenyang 110044, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 寻求替代含铬绝缘涂料的环保绝缘涂料。 方法 采用水溶性磷酸盐和水性树脂自制水性涂料,在无取向硅钢表面制备绝缘涂层,研究其固化工艺,并与国内涂料进行理化指标和涂层性能(附着力、表面电阻、耐腐蚀性能、耐热性)对比。 结果 自制绝缘涂料无刺激性气味,稳定性好,使用寿命长,在固化时间 20 ~24 s、固化温度 480 ~520 ℃的条件下,可在无取向硅钢表面制得均匀、光亮的银灰色绝缘涂层。 绝缘涂层附着力为 A 级,12 h 中性盐雾试验腐蚀面积低于 5% ,在 750 ℃ 高温退火 2 h 不掉粉,表面绝缘电阻为 297 Ω/ mm2(1. 0 ~1. 2 μm)。 结论 自制水性绝缘涂料为环保型单组分涂料,与国内绝缘涂料的涂层性能相当,满足国内钢厂产品技术要求。
英文摘要:
      Objective To seek environment-friendly insulating paint for replacing chromate coating. Methods A new chromatefree insulating coating on non-oriented silicon steel was prepared using self-made water-based paint composed of inorganic salt and water-soluble resin. The curing process of the insulating paint was studied, and the performance (adhesion, high temperature annealing, corrosion resistance and surface insulating resistance) of the insulating coating was analyzed in comparison with domestic coatings. Results The self-made paint had low offensive odor, good stability and long life; the insulating coating was light silver gray when the curing parameters were 20 ~24 s and 480 ~520 ℃; the adhesion force of the insulating coating was A; the corrosion area was less than 5% after 12 h salt spray; there was no coating desquamate after high-temperature annealing at 750 ℃ for 2 h; and the surface resistance was 297 Ω/ mm2(1. 0 ~ 1. 2 μm). Conclusion The self-made water-based paint was a one-component chromate-free paint, the performance of the insulating coating met the technical requirement of steel products, as good as that of domestic paints.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19497549位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号