张倩茹,傅戈雁.铁镍梯度材料抗低应力多冲碰撞塑性变形性能研究[J].表面技术,2014,43(6):28-32.
ZHANG Qian-ru,FU Ge-yan.Research of Resistance to Plastic Deformation of Iron-Nickel Gradient Materials under the Low and Repeated Impact Stress[J].Surface Technology,2014,43(6):28-32 |
| 铁镍梯度材料抗低应力多冲碰撞塑性变形性能研究 |
| Research of Resistance to Plastic Deformation of Iron-Nickel Gradient Materials under the Low and Repeated Impact Stress |
| 投稿时间：2014-07-02 修订日期：2014-12-10 |
| DOI： |
| 中文关键词: 低应力多冲碰撞 塑性变形 梯度材料 |
| 英文关键词:repeated impact under low stress plastic deformation gradient material |
| 基金项目:国家自然科学基金项目(11172191);江苏省科技支撑计划(BE2012068) |
|
|
|
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 研究梯度材料抗低应力多冲碰撞塑性变形能力。 方法 对纯铁材料、铁镍突变材料和铁镍梯度材料进行多次冲击碰撞试验,分析 3 种材料的累积变形量、不同层深处的应变和形变硬化程度、表面微观组织。 结果 总形变量、不同层深处的应变和形变硬化程度方面,纯铁材料略大于铁镍突变材料,远大于铁镍梯度材料。 铁镍突变材料和纯铁材料表层为单相多晶组织,且界面密度较小;铁镍梯度材料表层为多相多晶组织,且界面的密度大,其形变被抑制。 结论 铁镍梯度材料的抗低应力多冲碰撞塑性变形的能力最强,铁镍突变材料次之,纯铁材料最差。 |
| 英文摘要: |
| Objective To study the resistance to plastic deformation of iron-nickel gradient materials under the low and repeated impact stress. Methods Repeated impact tests were conducted on pure iron material, iron-nickel mutation material and iron-nickel gradient material. The cumulative deformation, strain and deformation hardening degree with different depths, and the surface microstructure were analyzed and compared. Results The total deformation, strain and deformation hardening degree with different depths of the pure iron material were a little larger than those of the iron-nickel mutation material, and much larger than those of the iron-nickel gradient material. The surface of the pure iron material and the iron-nickel mutation material was single-phase polycrystalline structure and the density of interface was small. The surface of the iron-nickel gradient material was multiphase polycrystalline structure, the density of interface was larger, and the plastic deformation was more suppressed. Conclusion For the resistance ability to plastic deformation under the low and repeated impact stress, the iron-nickel gradient material was the strongest, followed by the iron-nickel mutation material, and the pure iron material specimen was the worst. |
| 查看全文 查看/发表评论 下载PDF阅读器 |