李雅丽,付新,高锦红,刘娟.木质纤维表面改性对木塑复合材料力 学性能的影响[J].表面技术,2014,43(5):33-36.
LI Ya-li,FU Xin,GAO Jin-hong,LIU Juan.Effect of Lignocellulose Surface Characteristics on the Mechanical Properties of Wood-plastic Composites[J].Surface Technology,2014,43(5):33-36
木质纤维表面改性对木塑复合材料力 学性能的影响
Effect of Lignocellulose Surface Characteristics on the Mechanical Properties of Wood-plastic Composites
投稿时间:2014-04-16  修订日期:2014-06-19
DOI:
中文关键词:  玉米秸秆粉  表面接触角  表面张力  复合材料
英文关键词:corn stover fibers  surface contact angles  surface tension  composite material
基金项目:陕西省军民融合研究基金项目 ( 13JMR22) ; 渭南师范学院特色学科项目 ( 14TSXK04)
作者单位
李雅丽 渭南师范学院 化学与生命科学学院, 陕西 渭南 714000 
付新 渭南师范学院 化学与生命科学学院, 陕西 渭南 714000 
高锦红 渭南师范学院 化学与生命科学学院, 陕西 渭南 714000 
刘娟 渭南师范学院 化学与生命科学学院, 陕西 渭南 714000 
AuthorInstitution
LI Ya-li Collage of Chemistry and Life Sciences, Weinan Normal University, Weinan 714000, China 
FU Xin Collage of Chemistry and Life Sciences, Weinan Normal University, Weinan 714000, China 
GAO Jin-hong Collage of Chemistry and Life Sciences, Weinan Normal University, Weinan 714000, China 
LIU Juan Collage of Chemistry and Life Sciences, Weinan Normal University, Weinan 714000, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目 的 改善木质纤维与 热塑性塑料的界面相容性, 提高木塑复合材料的力 学性能。 方法 采用毛细管上升法测定不同 探测液在未改性玉米秸秆粉和硅烷偶联剂 改性玉米秸秆粉表面的 接触角 , 通过Owens 法计算玉米秸秆粉改性前后的表面张力及其分量。 结果 未改性玉米秸秆粉的表面张力 为 28. 88mN /m, 极性分量为 22. 20 mN /m; 而改性玉米秸秆粉的 表面张力 为 35. 69 mN /m, 极性分量为 3. 51 mN /m。 结论 在与 热塑性塑料复合时, 改性玉米秸秆粉有更好的 界面相容性, 其制 备的 木塑复合材料有更好的力学强度。
英文摘要:
      Objective To improve the interfacial compatibility of lignocellulose with thermoplastic plastics, and increase the mechanical properties of wood-plastic composites. Methods The contact angles of three probe liquids against unmodified and modified corn stover fibers were tested by capillary rise method, and the surface tension and its components of unmodified and modified corn stover fibers were calculated based on the method of Owens-wendt-Kaelble. Results The results showed that the surface tension of the unmodified corn stover fibers was 28. 88 mN/m and its polar component was 22. 20 mN/m, while the surface tension of the modified corn stover fibers was 35. 69 mN/m and its polar component was 3. 51 mN/m. Conclusion Modified corn stover fibers had better interfacial compatibility with thermoplastics, which was also confirmed by the better mechanical properties of wood-plastic composites.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第13594164位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: wjqkbm@163.com

渝公网安备 50010702501715号