谢华,陈东,黄健萌.双涂层界面接触应力分析[J].表面技术,2014,43(2):1-5,17.
XIE Hua,CHEN Dong,HUANG Jian-meng.Analysis of the Contact Stress at Interface of Double Coatings[J].Surface Technology,2014,43(2):1-5,17
双涂层界面接触应力分析
Analysis of the Contact Stress at Interface of Double Coatings
投稿时间:2013-10-24  修订日期:2014-04-10
DOI:
中文关键词:  双涂层  界面应力  有限元法
英文关键词:double coating  interface stress  finite element method
基金项目:国家杰出青年基金项目(51205062)
作者单位
谢华 福州大学, 福州 350002 
陈东 福州大学, 福州 350002 
黄健萌 福州大学, 福州 350002 
AuthorInstitution
XIE Hua Fuzhou University, Fuzhou 350002, China 
CHEN Dong Fuzhou University, Fuzhou 350002, China 
HUANG Jian-meng Fuzhou University, Fuzhou 350002, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 研究在接触应力作用下,双涂层的总厚度及厚度比对其界面应力的影响规律。 方法 采用有限元方法研究两个界面,即涂层与基底界面和涂层间界面的 Mises 应力突变量和界面最大剪应力。结果 总厚度一定时,涂层厚度比变化对涂层/ 基底界面应力的影响较小,而对涂层间界面应力的影响明显。 对于薄涂层,涂层间界面 Mises 应力突变量和最大剪应力随着中间层厚度比例的增大而减小;对于厚涂层,涂层间界面 Mises 应力突变量和最大剪应力随着中间层厚度比例的增大而减小。 涂层厚度比一定时,随着涂层总厚度增加,涂层间界面 Mises 应力突变量和最大剪应力先增大,后减小。 结论 双涂层的总厚度及厚度比对其界面应力有显著影响。
英文摘要:
      To investigate the influences of the coating thickness and interlayer-to-top layer coating thickness ratio tint:ttop on the interface stress in the TiN-interlayer coating/ substrate under contact stress. Methods Using Finite element method, the Mises stress gradient and the maximum shear stress at one interface between the coating and the base and the other between the top layer coating and the interlayer coating were studied. Results The coating thickness t and the interlayer-to-top layer coating thickness ratio tint : ttop had little influence on the interface stress between the coating and the base,however, they showed obvious influence on the interface stress between the top layer and the interlayer coating. For the thin coating, the Mises stress gradient and the maximum shear stress at the interface between the top layer and the interlayer were decreased when the interlayer-to-top layer coating thickness ratio tint : ttop increased, while for the thick coating, the Mises stress gradient and the maximum shear stress at the interface between the top layer and the interlayer were increased when the interlayer-to-top layer coating thickness ratio tint : ttop decreased. For the same interlayer-to-top layer coating thickness ratio tint:ttop, the Mises stress gradient and the maximum shear stress were first increased and then decreased when the coating thickness increased. Conclusion The coating thickness and the thickness ratio showed distinct influences on the interface stress of a double coating system.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第13565308位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: wjqkbm@163.com

渝公网安备 50010702501715号