沈远,刘京雷,侯峰,徐宏,任衍伦.偶联剂对氧化铁红粉体的表面改性[J].表面技术,2014,43(1):59-62.
SHEN Yuan,LIU Jing-lei,HOU Feng,XU Hong,REN Yan-lun.Surface Modification of Iron Oxide Red Powder Using Coupling Agent[J].Surface Technology,2014,43(1):59-62
偶联剂对氧化铁红粉体的表面改性
Surface Modification of Iron Oxide Red Powder Using Coupling Agent
投稿时间:2013-10-20  修订日期:2013-12-03
DOI:
中文关键词:  氧化铁红  表面改性  改性剂  亲油性
英文关键词:iron oxide red  surface modification  modifier  lipophilic property
基金项目:
作者单位
沈远 华东理工大学 机械与动力工程学院, 上海 200237 
刘京雷 华东理工大学 机械与动力工程学院, 上海 200237 
侯峰 华东理工大学 机械与动力工程学院, 上海 200237 
徐宏 华东理工大学 机械与动力工程学院, 上海 200237 
任衍伦 华东理工大学 机械与动力工程学院, 上海 200237 
AuthorInstitution
SHEN Yuan School of Mechanical and Power Engineering, East China University of Science and Technology, Shanghai 200237, China 
LIU Jing-lei School of Mechanical and Power Engineering, East China University of Science and Technology, Shanghai 200237, China 
HOU Feng School of Mechanical and Power Engineering, East China University of Science and Technology, Shanghai 200237, China 
XU Hong School of Mechanical and Power Engineering, East China University of Science and Technology, Shanghai 200237, China 
REN Yan-lun School of Mechanical and Power Engineering, East China University of Science and Technology, Shanghai 200237, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 研究硅烷偶联剂 KH-560 与钛酸酯偶联剂对氧化铁红粉体的改性效果。 方法 采用硅烷偶联剂 KH-560 与钛酸酯偶联剂对超细氧化铁红粉体进行改性,同时与未改性的粉体进行比较,对比研究粉体的亲油化度、吸油值、粒度分布、疏水性及分散情况。 结果 改性后,氧化铁红粉体的细化程度、团聚状况都有一定的改善。 粉体由改性前的亲水性变为亲油性,在有机体系中的分散性能得到了提高。 结论 硅烷偶联剂 KH-560 与钛酸酯偶联剂都能有效改善铁红粉体的表面性能,而钛酸酯偶联剂的改性效果优于 KH-560 。
英文摘要:
      Objective To study the modification effects of iron oxide powder by the silane coupling agent KH-560 and titanate coupling agent. Methods Fine iron oxide red powder after modification was compared with the unmodified powder. Lipophilic degree and oil-absorbed value were studied, and the modification effects were analyzed by CILAS particle size distribution analyzer, SEM and contact angle meters. Results The degree of refinement of iron oxide red powder was effectively improved and the agglomerates of the powder were reduced, the powder was changed from hydrophilic into lipophilic after modification, and the dispersing performance of the powder in the organic system was improved. Conclusion The two modifiers could effectively improve the surface performance of the fine iron oxide red powder. Besides, the modification effect of titanate coupling agent was better than that of KH-560.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第13565226位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: wjqkbm@163.com

渝公网安备 50010702501715号