肖健,鲁钢,冯述娟,苏武,赵霞,徐红,刘礼华.传能光纤表面低折射率光固化涂层的制备[J].表面技术,2013,42(6):97-100.
XIAO Jian,LU Gang,FENG Shu-juan,SU Wu,ZHAO Xia,XU Hong,LIU Li-hua.The Preparation of Low Refractive Index UV-curable Coatings for Transmitting Energy Fiber Surface[J].Surface Technology,2013,42(6):97-100
传能光纤表面低折射率光固化涂层的制备
The Preparation of Low Refractive Index UV-curable Coatings for Transmitting Energy Fiber Surface
投稿时间:2013-07-01  修订日期:2013-08-13
DOI:
中文关键词:  光纤涂料  折射率  吸光度  折射率
英文关键词:optical fiber coating  refractive index  absorbance  refractive index
基金项目:国家“863冶 基金项目(2013AA031502)
作者单位
肖健 南京工业大学 材料科学与工程学院, 南京 210009 
鲁钢 南京工业大学 材料科学与工程学院, 南京 210009 
冯述娟 江苏法尔胜光子有限公司, 江阴 214433 
苏武 江苏法尔胜光子有限公司, 江阴 214433 
赵霞 江苏法尔胜泓昇集团有限公司, 江阴 214433 
徐红 江苏法尔胜泓昇集团有限公司, 江阴 214433 
刘礼华 江苏法尔胜泓昇集团有限公司, 江阴 214433 
AuthorInstitution
XIAO Jian College of Material Science and Engineering, Nanjing University of Technology, Nanjing 210009 China 
LU Gang College of Material Science and Engineering, Nanjing University of Technology, Nanjing 210009 China 
FENG Shu-juan Jiangsu Fasten Photonics Co. , Ltd, Jiangyin 214433, China 
SU Wu Jiangsu Fasten Photonics Co. , Ltd, Jiangyin 214433, China 
ZHAO Xia Jiangsu Fasten Group Co. , Ltd, Jiangyin 214433, China 
XU Hong Jiangsu Fasten Group Co. , Ltd, Jiangyin 214433, China 
LIU Li-hua Jiangsu Fasten Group Co. , Ltd, Jiangyin 214433, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 制备低折射率光固化涂层。 方法 以全氟十一烷基丙烯酸酯( FA) 、甲基丙烯酸三氟乙酯( TRIFEMA) 、四氢呋喃丙烯酸酯 GM61 P00 ( THFA) 和聚氨酯丙烯酸酯( PU) 为主要组分,考察各组分用量对涂层接触角、吸光度和折射率的影响。 结果 在一定的用量范围内,折射率随 FA 和 TRIFEMA 用量增加而降低,随 THFA 和 PU 用量增加而升高;接触角随 FA 和 TRIFEMA 用量增加,先增大,然后保持稳定,随 THFA 和 PU 用量增加而减小;吸光度随 FA 用量增加而增大,随 TRIFEMA,THFA 和 PU 用量增加而减小。 结论 低折射率光固化涂料的最佳配比为 m( FA) : m( TRIFEMA) : m( THFA) : m( PU) = 2 :5 : 1 . 25 : 1 ,其涂层折射率为 1 . 387 ,吸光度为 0 . 0091 。
英文摘要:
      Objective The aim of this paper was to prepare the low-refractive index UV-curable coating. Methods 1 H,1 H, 11 H-perfluoroundecyl acrylate ( FA ) , Trifluoroethyl methacrylate ( TRIFEMA ) , Tetrahydrofurfuryl acrylate GM61 P00 ( THFA) and Polyurethane acrylate( PU) were used as the main ingredients, and their influences on the water contact angle, the absorbance of the film and the refractive index of the coating were investigated. Results Within a certain dosage range, the refractive index decreased with the increasing content of FA or TRIFEMA, and increased with the increase of THFA or PU; the contact angle increased and then remained stable with the increase of the FA and TRIFEMA, while it decreased when THFA and PU increased; the absorbance increased with increasing FA content,but when TRIFEMA, THFA and PU increased, the absorbance became lower. Conclusion The optimal proportion for the low-refractive index UV-curable coating was m( FA) : m( TRIFEMA) : m( THFA) : m( PU) = 2 : 5 : 1 . 25 :1 . Under this condition, the refractive index was 1 . 387 , and the absorbance was 0 . 0091 .
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19493915位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号