常会.壳聚糖-海藻酸钠吸附剂对电镀废水中 Cr( VI) 的吸附性能研究[J].表面技术,2013,42(5):84-88.
CHANG Hui.Study on the Adsorption Property of Chitosan-sodium Alginate Absorbent for Cr( VI) in Electroplating Waste Water[J].Surface Technology,2013,42(5):84-88
壳聚糖-海藻酸钠吸附剂对电镀废水中 Cr( VI) 的吸附性能研究
Study on the Adsorption Property of Chitosan-sodium Alginate Absorbent for Cr( VI) in Electroplating Waste Water
投稿时间:2013-05-30  修订日期:2013-06-24
DOI:
中文关键词:  CS-SA 吸附剂  电镀废水  Cr( VI)  吸附性能
英文关键词:CS-SA absorbent  electroplating waste water  Cr( VI)  adsorption properties
基金项目:
作者单位
常会 攀枝花学院, 攀枝花 617000 
AuthorInstitution
CHANG Hui Panzhihua University, Panzhihua 617000 , China 
摘要点击次数:
全文下载次数:
中文摘要:
      以天然壳聚糖( CS) 和海藻酸钠( SA) 为原料,在 CaCl2 作用下,制备了壳聚糖-海藻酸钠( CS-SA)吸附剂。 采用红外光谱仪对 CS-SA 吸附剂官能团进行表征,表明壳聚糖和海藻酸钠之间产生了静电吸引作用。以含低浓度 Cr( VI) 的电镀废水为处理对象,考察了 CS-SA 用量、吸附时间和 pH 值对 CS-SA 吸附性能的影响,同时对吸附动力学进行了研究。 结果表明:当 pH = 6 ,吸附时间为 120 min,CS-SA 用量为 0 . 15 g 时,离子去除率最高,达到了 98 . 86% ;吸附动力学最符合拟二级动力学方程。 解吸-再生实验表明,CS-SA 吸附剂可以再生使用。
英文摘要:
      A new kind of chitosan-sodium alginate absorbent was prepared using natural products chitosan and sodium alginate as raw material in the presence of CaCl2 . The functional groups of the CS-SA absorbent was characterized by FT-IR. The results show that chitosan and sodium alginate produce electrostatic attraction. The effects of CS-SA dosage, adsorption time and pH on adsorption property for low concentration Cr ( VI ) in electroplating wastewater were studied, and corresponding adsorption kinetics was investigated. The experimental results show that the adsorption rate can reaches 98 . 86 % under the optimal conditions of dosage 0 . 15 g, absorption time 120 min and pH 6 . The absorption kinetics accords with the pseudo-second-order equation. The desorption-regeneration experiment reveals that CS-SA adsorbent can regenerate and be reused.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第13565085位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: wjqkbm@163.com

渝公网安备 50010702501715号