430 不锈钢表面月桂酸自组装膜的探究
Research on the Lauric Acid SAMs on the Surface of 430 Stainless Steel
投稿时间:2012-12-20  修订日期:2013-01-28
DOI:
中文关键词:  430 不锈钢  月桂酸  自组装膜  缓蚀效率
英文关键词:430 stainless steel  lauric acid  SAMs  corrosion inhibition performance
基金项目:
作者单位
王海人 湖北大学 材料科学与工程学院, 武汉 430062 
陈凤 湖北大学 材料科学与工程学院, 武汉 430062 
屈钧娥 湖北大学 材料科学与工程学院, 武汉 430062 
聂德键 湖北大学 材料科学与工程学院, 武汉 430062 
AuthorInstitution
WANG Hai-ren Faculty of Materials Science and Engineering, Hubei University, Wuhan 430062 , China 
CHEN Feng Faculty of Materials Science and Engineering, Hubei University, Wuhan 430062 , China 
QU Jun-e Faculty of Materials Science and Engineering, Hubei University, Wuhan 430062 , China 
NIE De-jian Faculty of Materials Science and Engineering, Hubei University, Wuhan 430062 , China 
摘要点击次数:
全文下载次数:
中文摘要:
      采用浸泡法在 430 不锈钢表面制备了月桂酸自组装膜,通过电化学方法、接触角测试及微观形貌分析,研究了该自组装膜在 430 不锈钢表面的吸附行为及缓蚀作用。 研究结果表明:经过简单的浸泡,月桂酸分子能够稳定地吸附在不锈钢表面,自组装时间、组装液浓度以及基底表面前处理对组装膜的缓蚀效率有较大影响,自组装时间 4 h、月桂酸浓度 5 mmol / L、组装温度 35 ℃ 为最佳自组装条件;基底在组装之前进行钝化处理,有利于形成致密的自组装分子膜,提高不锈钢的耐蚀性能。
英文摘要:
      Self-assembled monolayers ( SAMs) of Lauric Acid ( LA) were prepared on the surfaces of 430 stainless steel (430 SS) by immersing method in the assembly solutions. The adsorption behavior and corrosion inhibition performance of LA SAMs were investigated by electrochemical tests, contact angle measurement and microscopic morphology analysis. The results indicated that LA SAMs was chemically absorded on 430 SS via a simply immersion progress. The assembly time of 4 h, LA concentration of 5 mmol / L,assembly temperature of 35 ℃ were the optimal parameters for assembling. Passivation pretreatment was beneficial for forming a denser SAMs on the surface of 430 SS and improving the corrodion resistance of 430 SS.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19502042位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号