卢燕,郑兴文,刘新露,曾凤春.硫酸介质中榕树叶提取液的缓蚀性能及其与 KI 的缓蚀协同效应[J].表面技术,2013,42(3):28-32.
LU Yan,ZHENG Xing-wen,LIU Xin-lu,ZENG Feng-chun.Corrosion Inhibition of Ficus Microcarpa Leaves Extract and Its Synergistic Effect with KI in Sulfuric Acid[J].Surface Technology,2013,42(3):28-32
硫酸介质中榕树叶提取液的缓蚀性能及其与 KI 的缓蚀协同效应
Corrosion Inhibition of Ficus Microcarpa Leaves Extract and Its Synergistic Effect with KI in Sulfuric Acid
投稿时间:2013-01-10  修订日期:2013-02-26
DOI:
中文关键词:  榕树叶  缓蚀剂  碳钢  硫酸  KI  协同效应
英文关键词:ficus microcarpa leaves  corrosion inhibitor  carbon steel  sulfuric acid  KI  synergistic effect
基金项目:材料腐蚀与防护四川省重点实验室项目(2011CL07) ;绿色催化四川省高校重点实验室项目( LYJ1102)
作者单位
卢燕 四川理工学院 化学与制药工程学院, 自贡 643000 
郑兴文 四川理工学院 化学与制药工程学院, 自贡 643000;材料腐蚀与防护四川省重点实验室, 自贡 643000 
刘新露 四川理工学院 化学与制药工程学院, 自贡 643000 
曾凤春 四川理工学院 化学与制药工程学院, 自贡 643000 
AuthorInstitution
LU Yan School of Chemical and Pharmaceutical Engineering,Sichuan University of Science & Engineering, Zigong 643000 ,China 
ZHENG Xing-wen School of Chemical and Pharmaceutical Engineering,Sichuan University of Science & Engineering, Zigong 643000 ,China;Key Laboratory of Material Corrosion and Protection of Sichuan Province, Zigong 643000 , China 
LIU Xin-lu School of Chemical and Pharmaceutical Engineering,Sichuan University of Science & Engineering, Zigong 643000 ,China 
ZENG Feng-chun School of Chemical and Pharmaceutical Engineering,Sichuan University of Science & Engineering, Zigong 643000 ,China 
摘要点击次数:
全文下载次数:
中文摘要:
      通过电化学方法和失重法,研究了榕树叶提取液( FLE) 对碳钢在硫酸溶液中的缓蚀性能,同时研究了它与 KI 的缓蚀协同效应,探讨了缓蚀机理。 研究结果表明:在硫酸溶液中,FLE 对碳钢属混合抑制型缓蚀剂,缓蚀效率随其浓度的增加而增大;FLE 与 KI 之间存在良好的协同效应,两者复配后,体系的腐蚀电流密度减小,电荷传递电阻增大,双电层电容减小,缓蚀效率增大,表现出更好的缓蚀作用;FLE 与 KI 复配前后,其在碳钢表面的吸附均为自发过程,且符合 Langmuir 吸附等温方程。
英文摘要:
      Through electrochemical methods and weight loss measurement, the corrosion inhibition of ficus microcarpa leaves extract ( FLE) for carbon steel in sulfuric acid solutions was studied, and the synergistic effect between FLE and KI was investigated, furthermore the inhibition mechanism of FLE was discussed. The results showed that FLE was a mixed-type inhibitor for carbon steel,and the inhibition efficiency of FLE for carbon steel increased with increase of the concentration of FLE.There existed significant synergistic effect between FLE and KI,which made the mixture of FLE and KI was used as corrosion inhibitor,the corrosion current density and double layer capacitance decreased, the charge transfer resistance increased, consequently showed better corrosion inhibition and higher inhibition efficiency. The adsorption of FLE with the presence and absence of KI on the carbon steel surface was a spontaneous process,and obeyed Langmuir adsorption isotherm model .
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19512440位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号