贾明子,张哲,阮乐,吴凤美.咪唑类化合物自组装膜对 316 不锈钢的缓蚀作用[J].表面技术,2013,42(3):23-27,41.
JIA Ming-zi,ZHANG Zhe,RUAN Le,WU Feng-mei.Corrosion Inhibition Action of Imidazole Derivatives Self-assembled Films for 316 Stainless Steel[J].Surface Technology,2013,42(3):23-27,41
咪唑类化合物自组装膜对 316 不锈钢的缓蚀作用
Corrosion Inhibition Action of Imidazole Derivatives Self-assembled Films for 316 Stainless Steel
  
DOI:
中文关键词:  咪唑类化合物  自组装膜  不锈钢  交流阻抗谱  极化曲线
英文关键词:imidazole derivatives  self-assembled films  stainless steel  EIS  polarization curves
基金项目:中文基金项目
作者单位
贾明子 桂林理工大学 化学与生物工程学院, 桂林 541004 
张哲 桂林理工大学 化学与生物工程学院, 桂林 541004;广西建筑新能源与节能重点实验室, 桂林 541004;广西高校应用化学新技术重点实验室, 桂林 541004 
阮乐 桂林理工大学 化学与生物工程学院, 桂林 541004 
吴凤美 桂林理工大学 化学与生物工程学院, 桂林 541004 
AuthorInstitution
JIA Ming-zi College of Chemistry and Bioengineering,Guilin University of Technology, Guilin 541004 , China 
ZHANG Zhe College of Chemistry and Bioengineering,Guilin University of Technology, Guilin 541004 , China;Key Laboratory on New Building Energy and Energy Conservation of Guangxi, Guilin 541004 , China;Key Laboratory on New Technique of Applied Chemistry of Universities of Guangxi, Guilin 541004 , China 
RUAN Le College of Chemistry and Bioengineering,Guilin University of Technology, Guilin 541004 , China 
WU Feng-mei College of Chemistry and Bioengineering,Guilin University of Technology, Guilin 541004 , China 
摘要点击次数:
全文下载次数:
中文摘要:
      通过电化学阻抗谱、极化曲线和量子化学方法,研究了在 0 . 5 mol / L 的硫酸溶液中,咪唑、十二烷基咪唑、苄基咪唑、苯并咪唑四种缓蚀剂自组装膜对 316 不锈钢的缓蚀性能。 研究结果表明:四种缓蚀剂均为阴极型缓蚀剂,对不锈钢具有较好的缓蚀作用,在 1 X10-3mol / L 的浓度下,随着组装时间的延长,自组装膜对不锈钢的缓蚀效率也相应增强,它们的缓蚀能力主要由最高占据轨道能 EHOMO的大小决定,缓蚀能力由大到小依次为苯并咪唑>十二烷基咪唑>苄基咪唑>咪唑。
英文摘要:
      The corrosion inhibition action of imidazole, 1-dodecylimidazole, 1-benzylimidazole, benzimidazole self-assembled films for 316 stainless steel in 0 . 5 mol / L H2SO4solution was investigated by electrochemical impedance spectroscopy,polarization curves and quantum chemical calculations. Results showed that four inhibitors were all cathodic inhibitors and performed pretty inhibiting efficiency for 316 stainless steel . As the concentration of inhibitors were 1 X10-3mol / L,the longer the assembled time,the better the effect of inhibition. The inhibition efficiency of the four inhibitors was up to the value of EHOMO. The inhibition efficiency of the four inhibitors decreased as follows:benzimidazole>1-dodecylimidazole>1-benzylimidazole> imidazole.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19513672位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号