硅烷偶联剂链长对纳米 TiO2表面改性的影响
Effect of Chain Length of Silane Coupling Agent for Surface Modification of Nano-TiO2
投稿时间:2012-11-20  修订日期:2012-10-30
DOI:
中文关键词:  硅烷偶联剂  链长  纳米 TiO2  表面改性
英文关键词:silane coupling agent  chain  nano-TiO2  surface modification
基金项目:江苏省水利科技项目(2012054)
作者单位
郝春静 中国矿业大学 环境与测绘学院, 徐州 221116 
湛含辉 中国矿业大学 环境与测绘学院, 徐州 221116 
王晓 中国矿业大学 环境与测绘学院, 徐州 221116 
AuthorInstitution
HAO Chun-jing School of Environment Science and Spatial Informatics,China University of Mining and Technology,Xuzhou 2 2 1 1 1 6,China 
ZHAN Han-hui School of Environment Science and Spatial Informatics,China University of Mining and Technology,Xuzhou 2 2 1 1 1 6,China 
WANG Xiao School of Environment Science and Spatial Informatics,China University of Mining and Technology,Xuzhou 2 2 1 1 1 6,China 
摘要点击次数:
全文下载次数:
中文摘要:
      采用具有不同链长的硅烷偶联剂 KH570 和 KH171 分别对纳米 TiO2 粒子进行了表面改性。 采用红外光谱( FT-IR) 、热重分析( TG) 、透射电镜( TEM) 和润湿性实验等测试。 结果表明:硅烷偶联剂有机链长的空间位阻效应对纳米粒子改性起关键作用。 TEM 表明经长链的 KH570 改性纳米 TiO2 分散效果更佳;热重分析和润湿性实验表明当长链 KH570 用量为 10% 时,纳米粒子表面接枝率和水接触角均达到最大,分别为 8. 05% 和 76. 6o;红外光谱表明长链的 KH570 键合强度较 KH171 大。
英文摘要:
      Nano-TiO2particles were modified respectively by silane coupling agent KH570 and KH171 with different chain length. The influence of KH570 and KH171 on the graft modifying effect of Nano-TiO2was studied by FT-IR, TG, TEM techniques . The results show that the organic chain length of silane coupling agent can produce space steric hindrance effect . It plays a key role on modification nanometer particles. TEM show that dispersion effect on modifying nano-TiO2by long-chain silane coupling agent( KH570 ) is much better. TG and wettability experiments show conent of long-chain silane coupling agent KH570 is 10 % , the coupling agent grafting rate and water contact angle is maximum, respectively 8 . 05 % and 76 . 6 o ; FT-IR show that long-chain KH570 bond strength is much stronger than KH171 .
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19502552位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号