柳鑫华,孙彩云,王庆辉,韩婕,佟欣佳.无磷海水缓蚀剂的开发[J].表面技术,2013,42(1):94-97.
LIU Xin-hua,SUN Cai-yun,WANG Qing-hui,HAN Jie,TONG Xin-jia.Development of Seawater Inhibitors without Phosphor[J].Surface Technology,2013,42(1):94-97
无磷海水缓蚀剂的开发
Development of Seawater Inhibitors without Phosphor
投稿时间:2012-10-29  修订日期:2012-11-19
DOI:
中文关键词:  钨酸盐  无磷缓蚀剂  海水  缓蚀性能
英文关键词:stungstate  non-phosphor corrosion inhibitor  sea water  corrosion inhibition property
基金项目:河北省科技局科技攻关项目(06213027)
作者单位
柳鑫华 河北联合大学 轻工学院, 唐山 063000 
孙彩云 河北联合大学 轻工学院, 唐山 063000 
王庆辉 河北联合大学 轻工学院, 唐山 063000 
韩婕 河北联合大学 轻工学院, 唐山 063000 
佟欣佳 河北联合大学 轻工学院, 唐山 063000 
AuthorInstitution
LIU Xin-hua College of Light Industry, Hebei United University, Tangshan 063000 , China 
SUN Cai-yun College of Light Industry, Hebei United University, Tangshan 063000 , China 
WANG Qing-hui College of Light Industry, Hebei United University, Tangshan 063000 , China 
HAN Jie College of Light Industry, Hebei United University, Tangshan 063000 , China 
TONG Xin-jia College of Light Industry, Hebei United University, Tangshan 063000 , China 
摘要点击次数:
全文下载次数:
中文摘要:
      通过失重法测定腐蚀速率,并计算缓蚀率,确定了具有较好协同缓蚀效应的四元无磷海水缓蚀剂配方,并通过电化学极化、SEM、 EDS 等分析手段,对该无磷海水复合缓蚀剂的缓蚀机理进行了研究。 结果表明:配方以 40 mg / L 钨酸盐+40 mg / L 葡萄糖酸盐+4 mg / L Zn2++30 mg / L 三乙醇胺为宜,该缓蚀剂在海水中对碳钢的缓蚀率超过 90% ;此无磷复合缓蚀剂为阳极型缓蚀剂,海水中添加了此缓蚀剂后,碳钢试片表面形成了以氧化铁为主要成分,同时含有钨和锌的混合型沉淀膜。
英文摘要:
      A quaternary corrosion inhibitor formula without phosphorus, which has a good synergistic effect was conformed in natural seawater through measuring corrosion rate and corrosion rate with the weight loss method. Corrosion mechanism of the compound corrosion inhibitors was studied through the electrochemical polarization, SEM and EDS analysis method. The results indicate that the inhibition efficiency is over 90 % in the proportion of 40 mg / L stungstate,40 mg / L sodium gluconate,4 mg / L Zn2+and 30 mg / L TEA. The compound inhibitor is an anodic corrosion inhibitor which formes a compact film on carbon steel surface, the main composition of the film is iron oxide with some W and Zn.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19992140位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号