何箐,李嘉,詹华,汪瑞军,王伟平.粘结层和陶瓷层厚度对纳米结构热障涂层性能的影响[J].表面技术,2013,42(1):17-20,41.
HE Qing,LI Jia,ZHAN Hua,WANG Rui-jun,WANG Wei-ping.Effects of Thickness of Bond Coat and Ceramic Coating on the Properties of Nano-structure Thermal Barrier Coatings[J].Surface Technology,2013,42(1):17-20,41
粘结层和陶瓷层厚度对纳米结构热障涂层性能的影响
Effects of Thickness of Bond Coat and Ceramic Coating on the Properties of Nano-structure Thermal Barrier Coatings
投稿时间:2012-10-16  修订日期:2012-11-24
DOI:
中文关键词:  热障涂层  陶瓷层厚度  层厚比  热循环寿命
英文关键词:thermal barrier coatings  thickness of ceramic coating  ratio of coating layer thickness  thermal cycle life
基金项目:
作者单位
何箐 中国农业机械化科学研究院 表面工程技术研究所, 北京 100083 
李嘉 中国农业机械化科学研究院 表面工程技术研究所, 北京 100083 
詹华 中国农业机械化科学研究院 表面工程技术研究所, 北京 100083 
汪瑞军 中国农业机械化科学研究院 表面工程技术研究所, 北京 100083 
王伟平 中国农业机械化科学研究院 表面工程技术研究所, 北京 100083 
AuthorInstitution
HE Qing Surface Engineering Research Institute, Chinese Academy of Agricultural Mechanization Sciences, Beijing 100083 , China 
LI Jia Surface Engineering Research Institute, Chinese Academy of Agricultural Mechanization Sciences, Beijing 100083 , China 
ZHAN Hua Surface Engineering Research Institute, Chinese Academy of Agricultural Mechanization Sciences, Beijing 100083 , China 
WANG Rui-jun Surface Engineering Research Institute, Chinese Academy of Agricultural Mechanization Sciences, Beijing 100083 , China 
WANG Wei-ping Surface Engineering Research Institute, Chinese Academy of Agricultural Mechanization Sciences, Beijing 100083 , China 
摘要点击次数:
全文下载次数:
中文摘要:
      采用超音速火焰喷涂+大气等离子喷涂工艺,在 K403 高温合金表面制备不同层厚比的 NiCrAlY /纳米 7 YSZ 热障涂层,研究了涂层厚度变化对热障涂层表面粗糙度、结合强度、热震性能和热循环寿命的影响规律。 结果表明:当粘结层厚度一定时,随着陶瓷层厚度的增加,其表面粗糙度增加,涂层结合强度下降;当粘结层厚度为 50 μm 时,热障涂层的抗热震性能随陶瓷层厚度增加而降低,粘结层厚度提高至 100 μm 时,热障涂层的抗热震性能随陶瓷层厚度增加先提高,后降低,热障涂层在 1100 ℃ 的热循环寿命测试结果也基本对应这一规律;当粘结层厚 50 μm 且陶瓷层 / 粘结层的层厚比在(1 ~ 2 ) 颐 1 的范围内,或者粘结层厚 100 μm 且陶瓷层 / 粘结层的层厚比在(2 ~ 2 . 5 ) 颐 1 范围内时,热障涂层具有较优异的性能。
英文摘要:
      The NiCrAlY+7 YSZ thermal barrier coatings( TBCs) with various thickness were prepared by High Velocity Oxygen-Fuel Spray( HVOF) and Atmosphere Plasma Spray( APS) on the surface of K403 superalloy, the effect of thicknesses of coating on the surface roughness, bond strength, thermal shock resistance, thermal cycle life of TBCs were studied. The results show that surface roughness increases and bond strength decreases with thickness of ceramic coating increasing, when the thickness of bond coat is 50 μm, thermal shock resistance and thermal cycle life are decreased with thickness of ceramic coating increasing. When the thickness of bond coat is 100 μm, the thermal shock resistance of TBC increases first and then reduces with the increase of thickness of the top layer, at the same time the thermal cycle life test result of TBC is to corresponded to that rule at 1100 ℃ . Depend on these tests, confirmed TBC of NiCrAlY / nano-7 YSZ exhibites excellent performance,when the thickness of bond coat is 50 μm and 100 μm, the ratio of thickness with top coating / bond coat is 2 to 1 and 2. 5 to 2 respectively.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19992420位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号