袁美华,古绪鹏,夏友谊,昌兴龙.聚苯胺与其它成膜物复配的成膜性和电导率研究[J].表面技术,2012,(6):115-117,127.
YUAN Mei-hua,GU Xu-peng,XIA You-yi,CHANG Xing-long.Study on Film-forming Property and Electrical Conductivity of Polyaniline and other Film Former[J].Surface Technology,2012,(6):115-117,127 |
| 聚苯胺与其它成膜物复配的成膜性和电导率研究 |
| Study on Film-forming Property and Electrical Conductivity of Polyaniline and other Film Former |
| 投稿时间：2012-06-26 修订日期：2012-12-20 |
| DOI： |
| 中文关键词: 聚苯胺 成膜性 电导率 |
| 英文关键词:polyaniline film forming electrical conductivity |
| 基金项目: |
|
|
|
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 将阳离子苯丙、水性环氧树脂、脲醛树脂两两复配成复合乳液,并与聚苯胺乳液进行混合,制得涂液,研究了复合乳液中成膜物的种类、浓度以及复合乳液与聚苯胺乳液的配比,对涂膜表观和电导率的影响。结果表明,采用阳离子苯丙与水性环氧树脂的复合乳液,并与聚苯胺乳液按质量比4 颐3 混合,得到的涂膜表观好,最高电导率可达0. 004 51 S/ cm。 |
| 英文摘要: |
| The cationic styrene-acrylic emulsion, waterborne epoxy emulsion and urea resin were compounded with each other and then the composite emulsion were mixed with polyaniline emulsion. The type and concentration of film former and the ratio of composite emulsion to polyaniline emulsion and their influences on the film-forming property and electrical conductivity were investigated. The results show that excellent film can be obtained when mass ratio of cationic styrene-acrylic and water-borne epoxy composite emulsion to polyaniline emulsion is 4 颐3 and maximum electrical conductivity can reach 0. 004 51 S/ cm |