黄凤祥,满瑞林,胡俊利,刘小勤,刘晶晶.彩色不锈钢板电化学褪膜工艺研究[J].表面技术,2012,(6):78-81,107.
HUANG Feng-xiang,MAN Rui-lin,HU Jun-li,LIU Xiao-qin,LIU Jing-jing.Study on Film-fading Process of Uneven Colored Stainless Steel[J].Surface Technology,2012,(6):78-81,107
彩色不锈钢板电化学褪膜工艺研究
Study on Film-fading Process of Uneven Colored Stainless Steel
投稿时间:2012-08-24  修订日期:2012-12-20
DOI:
中文关键词:  不锈钢  电化学褪膜  再着色
英文关键词:stainless steel  film-fading technology by electrolytic process  recolor
基金项目:中南大学中央高校基本科研业务费专项资金资助(2012zzts054)
作者单位
黄凤祥 中南大学化学化工学院, 长沙410083 
满瑞林 中南大学化学化工学院, 长沙410083 
胡俊利 中南大学化学化工学院, 长沙410083 
刘小勤 中南大学化学化工学院, 长沙410083 
刘晶晶 中南大学化学化工学院, 长沙410083 
AuthorInstitution
HUANG Feng-xiang School of Chemistry and Chemical Engineering, Central South University, Changsha 410083, China 
MAN Rui-lin School of Chemistry and Chemical Engineering, Central South University, Changsha 410083, China 
HU Jun-li School of Chemistry and Chemical Engineering, Central South University, Changsha 410083, China 
LIU Xiao-qin School of Chemistry and Chemical Engineering, Central South University, Changsha 410083, China 
LIU Jing-jing School of Chemistry and Chemical Engineering, Central South University, Changsha 410083, China 
摘要点击次数:
全文下载次数:
中文摘要:
      研究了着色生产中出现的不均匀彩色不锈钢板的电化学褪膜技术。通过褪膜试样的表面光泽度及再着色性能两方面,评价褪膜工艺的优劣。通过光反射率法和质量损失速率法确定最佳褪膜配方,并探讨了温度、电流密度对褪膜试样表面光泽度的影响。分别检测了褪膜后再着色试样的色差、耐蚀性及耐磨性,结果显示,褪膜再着色试样的色差小于0. 7,腐蚀速率为11. 5831 g/ (m2·h),耐摩擦次数达1950 次,与常规着色试样的性能相当,表明褪膜试样的再着色能力优良。
英文摘要:
      The film-fading technology by electrolytic process of uneven colored stainless steel plate in the production process was studied. The quality of film-fading technology was evaluated by brightness of sample and performance of recolored film-fading sample. The suitable solution of film-fading technology was evaluated by mass loss rate method and optical reflectance method, effect of temperature and current density on optical reflectance ratio of film-fading samples were discussed; The color uniformity, corrosion resistance, crocking resistance of recolored film-fading sample were tested. The experimental results show that the color difference is less than 0. 7, the weightlessness corrosion rate is 11. 5831 g/ (m2·h), the rubbing times up to 1950. They all indicate that the performance of recolored film-fading sample is as excellent as the conventional coloring sample.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19496610位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号