李永哲,李长青,宋巍.超声辐照对碳纳米管增强环氧树脂黏度和力学性能的影响[J].表面技术,2012,(5):73-76.
LI Yong-zhe,LI Chang-qing,SONG Wei.Effects of Ultrasonic Irradiation on Mechanical Properties and Viscosity of Carbon Nanotubes Reinforced Epoxy Resin[J].Surface Technology,2012,(5):73-76
超声辐照对碳纳米管增强环氧树脂黏度和力学性能的影响
Effects of Ultrasonic Irradiation on Mechanical Properties and Viscosity of Carbon Nanotubes Reinforced Epoxy Resin
投稿时间:2012-04-26  修订日期:2012-10-20
DOI:
中文关键词:  超声辐照  碳纳米管  环氧树脂  力学性能
英文关键词:ultrasonic irradiation  carbon nanotubes  epoxy resin  mechanical properties
基金项目:
作者单位
李永哲 装甲兵工程学院装备再制造工程系,北京100072 
李长青 装甲兵工程学院装备再制造工程系,北京100072 
宋巍 装甲兵工程学院装备再制造工程系,北京100072 
AuthorInstitution
LI Yong-zhe Department of Equipment Remanufacture Engineering, Academy of Armored Force Engineering, Beijing 100072, China 
LI Chang-qing Department of Equipment Remanufacture Engineering, Academy of Armored Force Engineering, Beijing 100072, China 
SONG Wei Department of Equipment Remanufacture Engineering, Academy of Armored Force Engineering, Beijing 100072, China 
摘要点击次数:
全文下载次数:
中文摘要:
      采用超声辐照处理多壁碳纳米管增强环氧树脂复合材料,分析了超声辐照条件对复合材料的黏度、力学性能及拉伸断口显微形貌的影响。结果表明:温度一定时,多壁碳纳米管增强环氧树脂体系的黏度随超声辐照时间的延长而逐渐降低;超声辐照时间为5min时,环氧树脂的拉伸强度、弯曲强度、拉伸剪切强度达到最大值,较处理前分别提高了37%,167%和86%;经超声辐照后,拉伸断口形貌显示出更多的韧性断裂特征。
英文摘要:
      The multi-walls carbon nanotubes reinforced epoxy resin was treated with ultrasonic irradiation. The effects of ultrasonic irradiation on the viscosity, mechanical properties and fracture morphologies of composites were investigated. The results show that at the same temperatures, the viscosity of multi-walls carbon nanotubes reinforced epoxy resin gradually decreases with the increasing of ultrasonic irradiation time; When the ultrasonic irradiation time is 5 min, the tensile strength, flexural strength and tensile shear strength of epoxy resin reach the highest value, which were increased respectively by 37%,167% and 86%; Ultrasonic irradiation can make the tensile fracture morphology show more ductile fracture characteristics.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19514627位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号