张敬尧,谈宇.Ni-P纳米晶镀层的摩擦学性能研究[J].表面技术,2012,(5):41-43.
ZHANG Jing-yao,TAN Yu.Study on Tribological Property of the Ni-P Nanocrystalline Coating[J].Surface Technology,2012,(5):41-43 |
| Ni-P纳米晶镀层的摩擦学性能研究 |
| Study on Tribological Property of the Ni-P Nanocrystalline Coating |
| 投稿时间：2012-05-03 修订日期：2012-10-20 |
| DOI： |
| 中文关键词: 纳米晶镀层 摩擦学性能 组织结构 去应力退火 |
| 英文关键词:nanocrystalline coating tribological property organize structure stress-off annealing |
| 基金项目:福州大学科技发展基金资助项目(2011-XQ-013) |
|
|
|
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 采用化学沉积方法获得了Ni-P纳米晶和非晶两种镀层,对镀态镀层进行低温去应力退火处理。分析了镀层成分和结构,研究了组织结构和退火工艺对镀层摩擦学性能的影响规律及其内在机制。结果表明:Ni-P纳米晶镀层的摩擦学性能明显优于同条件下(仅改变镀液中的络合剂)制备的非晶镀层,镀层磨损机制发生了变化;适当地去应力退火有助于进一步提高镀层的显微硬度,达到降磨减摩的效果。 |
| 英文摘要: |
| The two coatings of Ni-P amorphous and nanocrystalline structure were obtained by electroless plating. Moreover the as-deposited coatings were treated with stress-off annealing of low temperature. The composition and structure of the coatings were analyzed. Effects of anneal process and coating organize structure on tribological property of coating, as well as its inner mechanism, were studied. The result shows that the tribological property of Ni-P nanocrystalline coating is superior to that of amorphous one at the same condition(only changing the complex agent in the bath),and different wear mechanism between the two coatings is discovered too. The excellent friction and wear alleviation coating with higher micro-hardness is obtained owing to the proper anneal process. |