王励钊,李春福,曹文豪.电化学充氢条件下TWIP钢应力腐蚀敏感性的研究[J].表面技术,2012,(4):39-41.
WANG Li-zhao,LI Chun-fu,CAO Wen-hao.Study on Stress Corrosion Sensitivity of TWIP Steel on the Electrochemical Hydrogen Charging Condition.Surface Technology,2012,(4):39-41.
电化学充氢条件下TWIP钢应力腐蚀敏感性的研究
Study on Stress Corrosion Sensitivity of TWIP Steel on the Electrochemical Hydrogen Charging Condition
投稿时间:2012-03-16  修订日期:2012-08-20
DOI:
中文关键词:  TWIP钢  应力腐蚀开裂  应力腐蚀敏感性  氢脆
英文关键词:TWIP steel  stress corrosion cracking  stress corrosion sensitivity  hydrogen embrittlement
基金项目:
作者单位
王励钊 西南石油大学,成都610500 
李春福 西南石油大学,成都610500 
曹文豪 西南石油大学,成都610500 
AuthorInstitution
WANG Li-zhao Southwest Petroleum University, Chengdu 610500, China 
LI Chun-fu Southwest Petroleum University, Chengdu 610500, China 
CAO Wen-hao Southwest Petroleum University, Chengdu 610500, China 
摘要点击次数:
全文下载次数:
中文摘要:
      通过慢应变速率拉伸和观察断口形貌等方法,研究了TWIP钢在电化学充氢条件下的应力腐蚀敏感性。结果表明,在电化学充氢条件下,TWIP钢具有应力腐蚀敏感性。恒定应变速率6.67×10-6s-1时,具有单向奥氏体结构的TWIP钢有较小的应力腐蚀敏感性,具有形变孪晶的TWIP钢有较高的应力腐蚀敏感性。这是因为孪晶的形成导致氢在局部浓度更高,因而促进了局部塑性变形,降低了内氢压,导致TWIP钢的应力腐蚀敏感性上升。
英文摘要:
      By slow strain rate tensile and fracture morphology observation methods, the stress corrosion susceptibility of TWIP steel was studied in the electrochemical hydrogen charging. The results show that TWIP steel have stress corrosion sensitivity on hydrogen changed conditions.Under constrain strain rate of 6.67×10-6s-1,with one-way austenitic structure TWIP steel have smaller stress corrosion sensitivity, deformation twinshave TWIP steel have a higher stress corrosion sensitivity. This is because the formation of the twin lead to the hydrogen has higher concentration in some areas, so it promotes the local plastic deformation, reduces the hydrogen pressure and increases the stress corrosion sensitivity of the TWIP steel.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第6401897位访问者    渝ICP备10003521号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: wjqkbm@163.com

渝公网安备 50010702501715号