胡亚微,贺惠蓉,马养民.电化学沉积Ni-P基复合膜及其润湿性研究[J].表面技术,2012,(3):57-59.
HU Ya-wei,HE Hui-rong,MA Yang-min.Preparation and Wettability of Ni-P Based Composite Coating through Electrochemical Deposition[J].Surface Technology,2012,(3):57-59 |
| 电化学沉积Ni-P基复合膜及其润湿性研究 |
| Preparation and Wettability of Ni-P Based Composite Coating through Electrochemical Deposition |
| 投稿时间：2011-12-30 修订日期：2012-06-20 |
| DOI： |
| 中文关键词: Ni-P基复合膜 电化学沉积 润湿性 |
| 英文关键词:Ni-P-based composite coating electrochemical deposition wettability |
| 基金项目:陕西省自然科学基金(2011JQ2009);陕西省教育厅项目(11JK0561);陕西科技大学博士科研启动基金(BJ10-22);高等学校博士学科点专项科研基金新教师类资助课题(20116125120004) |
|
|
| Author | Institution |
| HU Ya-wei | Key Laboratory of Auxiliary Chemistry & Technology for Chemical Industry, Ministry of Education, Shaanxi University of Science & Technology, Xi'an710021, China |
| HE Hui-rong | Key Laboratory of Auxiliary Chemistry & Technology for Chemical Industry, Ministry of Education, Shaanxi University of Science & Technology, Xi'an710021, China |
| MA Yang-min | Key Laboratory of Auxiliary Chemistry & Technology for Chemical Industry, Ministry of Education, Shaanxi University of Science & Technology, Xi'an710021, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 采用电化学沉积法于金属基体上制备Ni-P基复合膜,研究了复合膜表面修饰低表面能物质FAS后的润湿性能。对所制备的复合膜的显微结构和成分进行表征,并考察了TiO2 纳米粒子的加入对Ni-P基复合膜表面形貌和润湿性能的影响。结果表明:未添加TiO2 纳米粒子的Ni-P复合膜表面比较平坦,而Ni-P-TiO2 复合膜的表面呈现粗糙结构,经表面修饰后,Ni-P-TiO2 复合膜的疏水性能优于Ni-P复合膜。 |
| 英文摘要: |
| The Ni-based composite coatings were prepared through electrochemical deposition method, and their wettabilities were studied after modified with low-surface-energy material FAS. The morphology and component of asprepared coatings were characterized and the effect of TiO2 nanoparticles on morphology and wettability was investigated. The results indicated that the Ni-P-TiO2 coating displayed micro- and nano-structure and Ni-P coating had a more flat surface. The Ni-P-TiO2 coating showed better superhydrophobicity than Ni-P composite coating after modified with FAS. |