王良洪,谢红希,肖刚锋.7075铝合金化学镀Ni-P/Ni-W-P双层镀层研究[J].表面技术,2012,(2):43-46.
WANG Liang-hong,XIE Hong-xi,XIAO Gang-feng.Research of the Electroless Ni-P/Ni-W-P Duplex Coatings on 7075 Aluminium Alloy[J].Surface Technology,2012,(2):43-46
7075铝合金化学镀Ni-P/Ni-W-P双层镀层研究
Research of the Electroless Ni-P/Ni-W-P Duplex Coatings on 7075 Aluminium Alloy
投稿时间:2012-01-08  修订日期:2012-04-20
DOI:
中文关键词:  铝合金  Ni-P/Ni-W-P膜  化学镀  热处理  显微硬度
英文关键词:aluminium alloy  Ni-P/Ni-W-P coatings  electroless plating  heat treatment  microhardness
基金项目:
作者单位
王良洪 华南理工大学机械与汽车工程学院,广东510640 
谢红希 华南理工大学机械与汽车工程学院,广东510640 
肖刚锋 华南理工大学机械与汽车工程学院,广东510640 
AuthorInstitution
WANG Liang-hong School of Mechanical & Automotive Engineering, South China University of Technology, Guangdong 510640, China 
XIE Hong-xi School of Mechanical & Automotive Engineering, South China University of Technology, Guangdong 510640, China 
XIAO Gang-feng School of Mechanical & Automotive Engineering, South China University of Technology, Guangdong 510640, China 
摘要点击次数:
全文下载次数:
中文摘要:
      以7075铝合金为基体,采用直接连续化学镀法制备Ni-P/Ni-W-P双层膜,并采用SEM,EPMA,XRD和显微硬度计、电化学工作站等对膜层热处理前后的表(断)面形貌、成分、结构、硬度和耐腐蚀等性能进行了研究。结果表明:获得了致密无孔且与基体及层间相互结合紧密的非晶态Ni-P/Ni-W-P膜;热处理后,镀层硬度提高,而耐蚀性略有降低。
英文摘要:
      The electroless Ni-P/Ni-W-P duplex coatings were deposited directly on 7075 aluminium alloy. The morphology of surface and cross-section, composition, structure, microhardness and corrosion properties of coating before and after heat treating were studied by SEM,EPMA,XRD, microhardness tester, electrochemical workstation. The result shows that amorphousNi-P/Ni-W-P duplex coatings with good adhesion between interfaces and the substrate fully covered without pores are got.The hardness is improved and corrosion properties are a little decreased after heat treatment.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19497933位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号