陈枭,王洪涛,刘长华.20G 钢表面制备耐熔融铝硅合金腐蚀涂层的研究[J].表面技术,2012,(1):102-105.
CHEN Xiao,WANG Hong-tao,LIU Chang-hua.Research on Molten Al-Si Alloy Corrosion Resistant Coatings Prepared on 20G Steel Surface.Surface Technology,2012,(1):102-105.
20G 钢表面制备耐熔融铝硅合金腐蚀涂层的研究
Research on Molten Al-Si Alloy Corrosion Resistant Coatings Prepared on 20G Steel Surface
投稿时间:2011-10-20  修订日期:2012-02-20
DOI:
中文关键词:  铝硅合金  腐蚀  涂层  热震  附着力
英文关键词:Al-Si alloy  corrosion  coating  thermal shocking  adhesion
基金项目:江西省自然科学基金项目(2010GQC0117);江西省教育厅科技项目(GJJ11236)
作者单位
陈枭 九江学院机械与材料工程学院,九江332005 
王洪涛 九江学院机械与材料工程学院,九江332005 
刘长华 九江学院机械与材料工程学院,九江332005 
AuthorInstitution
CHEN Xiao School of Mechanical & Materials Engineering, Jiujiang University, Jiujiang 332005, China 
WANG Hong-tao School of Mechanical & Materials Engineering, Jiujiang University, Jiujiang 332005, China 
LIU Chang-hua School of Mechanical & Materials Engineering, Jiujiang University, Jiujiang 332005, China 
摘要点击次数:
全文下载次数:
中文摘要:
      太阳能热发电中,熔融铝硅合金储能材料会对换热管造成一定的腐蚀,为了延长换热管的使用寿命,在其表面制备了C1,C2和C3三种涂层,并对三种涂层的抗热震性能、附着力和耐熔融铝硅合金腐蚀性能进行了研究。结果发现:三种涂层具有较好的抗热震性能和附着力,在经过1080h熔融铝硅合金腐蚀试验后发现,C3涂层具有最好的耐腐蚀能力,涂覆C3涂层的20G钢基体的腐蚀层厚度,相对于无涂层20G钢基体降低了93.69%。
英文摘要:
      Molten Al-Si alloy phase change material would produce a certain corrosion to the heat exchange tube in solar thermal power generation integration system. C1, C2 and C3 protective coatings were prepared to enhance the life of 20G heat exchange tube. The properties of thermal shock resistance, adhesion and anti-corrosion of coatings were also studied. Results show that three coatings have good thermal shock resistant and adhesion properties, and C3 coating has the best capability of anti-corrosion after 1080h corrosion test. Compared with 20G steel substrate, the thickness of corrosion layer of 20G steel sprayed C3 coating drops 93.69%.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第6401992位访问者    渝ICP备10003521号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: wjqkbm@163.com

渝公网安备 50010702501715号