李刚,赵云龙,唐明忠.铝合金电子束表面改性层组织结构及腐蚀性能[J].表面技术,2012,(1):48-50,53.
LI Gang,ZHAO Yun-long,TANG Ming-zhong.Micro-structure and Corrosion Resistance of Irradiated by the HCPEB on LY12 Aluminum Alloy Surface.Surface Technology,2012,(1):48-50,53.
铝合金电子束表面改性层组织结构及腐蚀性能
Micro-structure and Corrosion Resistance of Irradiated by the HCPEB on LY12 Aluminum Alloy Surface
投稿时间:2011-10-14  修订日期:2012-02-20
DOI:
中文关键词:  电子束  LY12  表面改性  电化学腐蚀
英文关键词:lectron beam  LY12  surface modification  electrochemical corrosion
基金项目:
作者单位
李刚 辽宁工程技术大学材料科学与工程学院,阜新123000 
赵云龙 辽宁工程技术大学材料科学与工程学院,阜新123000 
唐明忠 辽宁工程技术大学材料科学与工程学院,阜新123000 
AuthorInstitution
LI Gang College of Material Science and Engineering, Liaoning Technical University, Fuxin 123000, China 
ZHAO Yun-long College of Material Science and Engineering, Liaoning Technical University, Fuxin 123000, China 
TANG Ming-zhong College of Material Science and Engineering, Liaoning Technical University, Fuxin 123000, China 
摘要点击次数:
全文下载次数:
中文摘要:
      对LY12铝合金表面进行高能电子束轰击改性处理,结果表明,合金表面出现熔坑,随轰击次数增加,熔坑数量减少,但直径变大。XRD分析得出,处理后,改性层中存在α-Al和第二相CuMgAl2,CuAl2,重熔层再结晶有择优取向。电化学腐蚀实验显示,经过轰击处理后,自腐蚀电位可从-626.92mV 提高到-523.33mV,自腐蚀电流由1.09×10-7 A 降低至3.12×10-9 A,耐腐蚀性能有明显提高。
英文摘要:
      The results that modification on LY12 aluminum alloy surface by high current pulse electron beam (HCPEB)indicate that there are many pits on LY12 aluminum alloy surface, the number of melting pit decrease and the diameter get bigger with the time of irradiation increasing. According to XRD analysis, some phrase such as α-Al,CuMgAl2 and CuAl2 are found in the melted layer treated by HCPEB and the melted layer recrystallization have preferred orientation. The result of electrochemical corrosion experiment show that the LY12 samples after treatment have better corrosion resistance than the matrix, corrosion potential increases from - 626.92mV to - 523.33mV and corrosion current decreases from 1.09×10-7 A to 3.12×10-9 A, corrosion resistance is improved obviously.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第6402089位访问者    渝ICP备10003521号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: wjqkbm@163.com

渝公网安备 50010702501715号