严春进,杨峻,崔浩然.节能型搪瓷涂层烧成工艺及其性能研究[J].表面技术,2012,(1):44-47.
YAN Chun-jin,YANG Jun,CUI Hao-ran.The Sintering Process and Performance Study on Energy-efficient Enamel Coating.Surface Technology,2012,(1):44-47.
节能型搪瓷涂层烧成工艺及其性能研究
The Sintering Process and Performance Study on Energy-efficient Enamel Coating
投稿时间:2011-11-23  修订日期:2012-02-20
DOI:
中文关键词:  搪瓷层  耐酸性能  抗机械冲击性能  耐温急变性能  有限元分析
英文关键词:enamel coating  acid corrosion resistance  impact resistance  thermal shock resistance  finite element analysis
基金项目:江苏省重大科技成果转化资金项目(BA2009006)
作者单位
严春进 南京工业大学机械与动力工程学院,南京210009 
杨峻 南京工业大学机械与动力工程学院,南京210009 
崔浩然 南京工业大学机械与动力工程学院,南京210009 
AuthorInstitution
YAN Chun-jin School of Mechanical and Power Engineering, Nanjing University of Technology,Nanjing 210009,China 
YANG Jun School of Mechanical and Power Engineering, Nanjing University of Technology,Nanjing 210009,China 
CUI Hao-ran School of Mechanical and Power Engineering, Nanjing University of Technology,Nanjing 210009,China 
摘要点击次数:
全文下载次数:
中文摘要:
      介绍了一种低温搪瓷釉的助熔剂,有效将搪瓷的烧成温度降至800℃以下,研究了烧成温度和保温时间对搪瓷层耐酸性能、抗机械冲击性能以及耐温急变性能的影响。结果表明:所制备搪瓷层的耐酸性能、抗冲击性能以及耐温急变性能都达到了国家优等品的标准,随着烧结温度的提高和保温时间的延长,搪瓷层的耐酸性能和抗机械冲击性能均提高。最后,运用有限元分析软件ANSYS分析了搪瓷层的传热性能,以及热应力对搪瓷层稳定性的影响。
英文摘要:
      A flux of low-temperature enamel glaze was introduced, with which the sintering temperature of the enamel was put down to 800℃. The effects of sintering temperature and holding time on the acid corrosion resistance, impact resistance and thermal shock resistance of enamel coating were investigated. The experiment results showed that the acid corrosion resistance, impact resistance and thermal shock resistance had all reached to the national superior product standard, and the acid corrosion resistance and impact resistance were improved with the increase of sintering temperature and holding time. At the end, the effect of thermal conduction and thermal stress on enamel coating stability was investigated with the commercial software ANSYS.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第6402123位访问者    渝ICP备10003521号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: wjqkbm@163.com

渝公网安备 50010702501715号