时海芳,郜世喜,李智超.坡缕石对三元硼化物陶瓷涂层磨损性能的影响[J].表面技术,2012,(1):41-43.
SHI Hai-fang,GAO Shi-xi,LI Zhi-chao.Effect of Palygorskite on Wear Performance of Mo2FeB2.Surface Technology,2012,(1):41-43.
坡缕石对三元硼化物陶瓷涂层磨损性能的影响
Effect of Palygorskite on Wear Performance of Mo2FeB2
投稿时间:2011-08-16  修订日期:2012-02-20
DOI:
中文关键词:  三元硼化物陶瓷涂层  坡缕石  耐磨性
英文关键词:ernary boride ceramic coating  palygorskite  abrasionresistance
基金项目:辽宁省一般项目(L2010160)
作者单位
时海芳 辽宁工程技术大学材料加工与表面技术研究所,阜新123000 
郜世喜 辽宁工程技术大学材料加工与表面技术研究所,阜新123000 
李智超 辽宁工程技术大学材料加工与表面技术研究所,阜新123000 
AuthorInstitution
SHI Hai-fang Institute of Materials Processing and Surface Technology, Liaoning Technical University, Fuxin 123000, China 
GAO Shi-xi Institute of Materials Processing and Surface Technology, Liaoning Technical University, Fuxin 123000, China 
LI Zhi-chao Institute of Materials Processing and Surface Technology, Liaoning Technical University, Fuxin 123000, China 
摘要点击次数:
全文下载次数:
中文摘要:
      采用热化学反应热喷涂技术,向骨料中加入坡缕石制得喷涂喂料粉末,在Q235钢表面制备含坡缕石的三元硼化物陶瓷涂层,观察了涂层的显微组织,测试了涂层的耐磨性能,分析了坡缕石对三元硼化物陶瓷涂层显微组织和耐磨性的影响。结果表明:坡缕石的添加,使得涂层变得致密且具有一定减摩效果;坡缕石的添加量占骨料总质量的2%时,所得三元硼化物陶瓷涂层的耐磨性比未加坡缕石时平均提高4倍。
英文摘要:
      Spraying feeding powder was produced through adding palygorskite. Ternary boride ceramic coating containing palygorskite was prepared by thermochemical reactive thermal spaying on Q235 steel substrate. The micro-structure of coating was observed, and the wear-resistance performance of coating was tested. The influence of palygorskite on microstructure and wear-resistance of ternary boride ceramic coating was analyzed. The results show that coating become compact and anti-friction because of adding palygorskite. When the adding dosage of palygorskite is 2% of the total aggregate quality, the abrasion resistance of coating has increased 4 times averagely than the coating without paly-gorskite
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第6401894位访问者    渝ICP备10003521号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: wjqkbm@163.com

渝公网安备 50010702501715号