殷锦捷,周华利.有机硅和环氧树脂复合改性聚氨酯涂料的研制[J].表面技术,2010,39(6):93-96.
YIN Jin-jie,ZHOU Hua-li.Preparation of Organosilicon and Epoxy Resin Modified Polyurethane Coating[J].Surface Technology,2010,39(6):93-96
有机硅和环氧树脂复合改性聚氨酯涂料的研制
Preparation of Organosilicon and Epoxy Resin Modified Polyurethane Coating
投稿时间:2010-07-01  修订日期:2010-12-10
DOI:
中文关键词:  聚氨酯涂料  有机硅  环氧树脂  复合改性
英文关键词:polyurethane coating  organosilicon  epoxy resin  compound modification
基金项目:
作者单位
殷锦捷 辽宁工程技术大学材料科学与工程学院,阜新123000 
周华利 辽宁工程技术大学材料科学与工程学院,阜新123000 
AuthorInstitution
YIN Jin-jie Institute of Material Science and Engineering, Liaoning Technical University, Fuxin 123000, China 
ZHOU Hua-li Institute of Material Science and Engineering, Liaoning Technical University, Fuxin 123000, China 
摘要点击次数:
全文下载次数:
中文摘要:
      通过单因素实验和正交实验,以涂膜的拉伸强度为依据,确定了用有机硅和环氧树脂复合改性聚氨酯涂料时,制备聚氨酯预聚体的单体甲苯二异氰酸酯(TDI)和聚醚二元醇(DL2000)的恰当配比,有机硅、环氧树脂和增塑剂的恰当添加量,以及恰当的反应时间和反应温度。对复合改性涂膜进行了红外光谱分析和热重分析,对比检测了未改性涂料、有机硅改性涂料、有机硅和环氧树脂复合改性涂料的各方面性能。结果表明,有机硅和环氧树脂复合改性的聚氨酯涂料各方面性能良好,涂膜具有较高的力学强度、良好的附着力、较低的吸水率、较好的热稳定性和耐酸碱性能。
英文摘要:
      By single factor experiment and the orthogonal experiment, organosilicon and epoxy resin modified polyurethane coating was prepared.According to the tensile strength of film, the optimum ratio of TDI and DL2000 of polyurethane was determined, appropriate additive quantity for organosilicon, epoxy resin and plasticizer was obtained, included suitable reaction time and reaction temperature. Infrared spectrum analysis and thermogravimetric analysis were tested for compound modification film, comparing various aspects of the performance with unmodified coating, organsilicone-modified coating and organosilicon and epoxy resin modified polyurethane coating. The result shows that organosilicon and epoxy resin modified polyurethane coating has high strength and adhesion force, low water adsorption rate, high thermal stability and corrosive acid and base resistance.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19500014位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号