谭延江,邓爱明,吴茜,林牧春,杨骐.硅烷偶联剂对羰基铁粉电磁性能的影响[J].表面技术,2010,39(5):68-71.
TAN Yan-jiang,DENG Ai-ming,WU Qian,LIN Mu-chun,YANG Qi.Effect of Silane Coupling Agent on Electromagnetic Property of Carbonyl Iron Powder[J].Surface Technology,2010,39(5):68-71
硅烷偶联剂对羰基铁粉电磁性能的影响
Effect of Silane Coupling Agent on Electromagnetic Property of Carbonyl Iron Powder
投稿时间:2010-06-03  修订日期:2010-10-10
DOI:
中文关键词:  羰基铁粉  乙烯基三甲氧基硅烷  电磁性能  改性
英文关键词:carbonyl iron powder  vinyltrimethoxysilane  electromagnetic property  modification
基金项目:
作者单位
谭延江 中国兵器工业第五九研究所,重庆400039 
邓爱明 中国兵器工业第五九研究所,重庆400039 
吴茜 中国兵器工业第五九研究所,重庆400039 
林牧春 中国兵器工业第五九研究所,重庆400039 
杨骐 中国兵器工业第五九研究所,重庆400039 
AuthorInstitution
TAN Yan-jiang No.59 Institute of China Ordnance Industry, Chongqing 400039, China 
DENG Ai-ming No.59 Institute of China Ordnance Industry, Chongqing 400039, China 
WU Qian No.59 Institute of China Ordnance Industry, Chongqing 400039, China 
LIN Mu-chun No.59 Institute of China Ordnance Industry, Chongqing 400039, China 
YANG Qi No.59 Institute of China Ordnance Industry, Chongqing 400039, China 
摘要点击次数:
全文下载次数:
中文摘要:
      利用FT-IR,SEM和矢量网络分析仪等对羰基铁粉改性前后的化学键特性、微观形貌和电磁参数等进行了研究,实验结果表明:硅烷偶联剂在羰基铁粉表面形成不均匀包覆层;羰基铁粉的电磁参数随硅烷偶联剂用量的增加而变化;根据电磁参数对材料的吸波性能进行计算,当乙烯基三甲氧基硅烷用量为2.0%(质量分数,后同)时,得到的吸波效果最好,5.2~ 10.0 GHz反射率均小于- 10 dB。
英文摘要:
      The chemical-bond characteristic,micro-structure and electromagnetic parameters were investigated by means of FT-IR,SEM and vector network analyzer. The results show that the vinyltrimethoxysilane integrates asymme- try deposits on the surface of the carbonyl iron powder, the electromagnetic parameters are variable as the quantity of si- lane coupling agent increases. According to the electromagnetic parameters, the absorbing property of carbonyl iron powder was computed. When the quantity of vinyltrimethoxysilane is 2.0%, the radar absorbing property is best, the frequency range with reflectivity under- 10 dB is from 5.2 GHz to 10.0 GHz.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19849583位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号