许斌,刘春明,郝建军,安成强.酸洗缓蚀剂对冷轧钢板磷化处理的影响[J].表面技术,2010,39(5):48-50.
XU Bin,LIU Chun-ming,HAO Jian-jun,AN Cheng-qiang.The Influence of Corrosion Inhibitor for Pickling on Phosphating of Cold-roll Steel Sheets[J].Surface Technology,2010,39(5):48-50
酸洗缓蚀剂对冷轧钢板磷化处理的影响
The Influence of Corrosion Inhibitor for Pickling on Phosphating of Cold-roll Steel Sheets
  修订日期:2010-10-10
DOI:
中文关键词:  冷轧钢板  酸洗  缓蚀剂  磷化
英文关键词:cold-rolled steel sheets  pickling  corrosion inhibitor  phosphating
基金项目:
作者单位
许斌 1.东北大学材料与冶金学院,沈阳110819;2.河北钢铁集团邯钢公司,邯郸056015 
刘春明 东北大学材料与冶金学院,沈阳110819 
郝建军 1.沈阳理工大学环境与化工学院,沈阳110159; 2.东北大学金属防护技术工程研究中心,沈阳110819 
安成强 1.沈阳理工大学环境与化工学院,沈阳110159; 2.东北大学金属防护技术工程研究中心,沈阳110819 
AuthorInstitution
XU Bin 1.School of Materials and Metallurgy, Northeastern University, Shenyang 110819, China;2.Hebei Iron& Steel Group Co. Ltd, Hebei,Handan 056015, China 
LIU Chun-ming School of Materials and Metallurgy, Northeastern University, Shenyang 110819, China 
HAO Jian-jun 1.School of Environment& Chemical Engineering, Shenyang Ligong University, Shenyang 110159, China;2.Engineering Research Center of Metal Protection Technology, Northeastern University, Shenyang 110819, China 
AN Cheng-qiang 1.School of Environment& Chemical Engineering, Shenyang Ligong University, Shenyang 110159, China;2.Engineering Research Center of Metal Protection Technology, Northeastern University, Shenyang 110819, China 
摘要点击次数:
全文下载次数:
中文摘要:
      采用乌洛托品、硫脲、乌洛托品-碘化钾、硫脲-硫酸铝4种酸洗缓蚀剂,在不同浓度的条件下对冷轧钢板进行酸洗,再对酸洗的钢板进行磷化处理,研究了酸洗缓蚀剂对磷化膜外观形貌、厚度、耐蚀性的影响。结果表明:酸洗液中使用不同的缓蚀剂对磷化膜外观、膜重与耐蚀性有明显的影响,乌洛托品和硫脲-硫酸铝的影响低于硫脲和乌洛托品-碘化钾;乌洛托品、硫脲、硫脲-硫酸铝在酸洗液中的质量分数分别不高于0.3%,1.0%,1.5%时,满足使用要求。
英文摘要:
      Using different concentrations of four pickling corrosion inhibitor, that included the methenamine, thiourea, methenamine-potassium iodide and thiourea-aluminum sulfate, first cold-rolled steel sheets were cleaned by pickling, then they were phophated by acid.In this time,theinfluence of differentpickling corrosioninhibitoron the appearance,the coating hardness and the corrosion resistance of phosphating films were researched. The result shows that the influence of different corrosion inhibitor is obvious for the appearance, the coating hardness and the corrosion resistance of phosphating films in pickling solutions. The influence of methenamine and thiourea-aluminum sulfate for phosphating films is lower than the influence of thiourea and methenamine-potassium iodide. The phosphating is suitable when corrosion inhibitor' s using concentration is no more than 0.3%,1.0%, 1.5% for methenamine, thiourea, and thiourea-aluminum sulfate.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19850267位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号