张国光,吴宗南,李琴,刘长虹,刘婷.电泳沉积法制备羟基磷灰石涂层[J].表面技术,2008,37(6):61-62,93.
ZHANG Guo-guang,WU Zong-nan,LI Qin,LIU Chang-hong,LIU Ting.Fabrication of HA Coating by Electrophoretic Deposition[J].Surface Technology,2008,37(6):61-62,93
电泳沉积法制备羟基磷灰石涂层
Fabrication of HA Coating by Electrophoretic Deposition
投稿时间:2008-08-05  修订日期:2008-12-10
DOI:
中文关键词:  羟基磷灰石  生物材料  电泳沉积  ζ电位
英文关键词:Hydroxyapatite  Biomaterial  Electrophoretic deposition  ζ potential
基金项目:国家自然科学基金( 50672100);江西省教育厅科技项目([ 2006] 155,[ 2006] 313)
作者单位
张国光 南昌航空大学材料科学与工程学院,江西南昌330063 
吴宗南 南昌航空大学材料科学与工程学院,江西南昌330063 
李琴 南昌航空大学材料科学与工程学院,江西南昌330063 
刘长虹 南昌航空大学材料科学与工程学院,江西南昌330063 
刘婷 南昌航空大学材料科学与工程学院,江西南昌330063 
AuthorInstitution
ZHANG Guo-guang School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063, China 
WU Zong-nan School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063, China 
LI Qin School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063, China 
LIU Chang-hong School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063, China 
LIU Ting School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063, China 
摘要点击次数:
全文下载次数:
中文摘要:
      羟基磷灰石是一种最有发展前途的生物材料之一。采用电泳沉积方法分别在T16A14V基体和电泳沉积的HA/Ti02复合涂层上制备了HA生物陶瓷涂层。将HA粉体分散到正丁醇溶液中,通过测量zeta电位确定了悬浮体系中三乙醇胺和HA的含量。研究发现:HA沉积量随沉积温度和沉积电压的增加而增加,随沉积时间延长呈线性增长。对沉积量与电泳沉积工艺参数的关系进行了理论探讨。SEM结果表明,采用二次电泳沉积在HA/Ti02涂层表面制备的HA涂层更加致密、平整。
英文摘要:
      Hydroxyapatite is one of the most hopeful biomedical materials. Hydroxyapatite ( HA) coatings on the Ti6A14V and HA/Ti02 composite substrates were obtained by electrophoretic deposition process. Zeta potential was used to determine the content of triethanolamine and HA particles in the stable butyl alcohol suspension. HA deposit yields increased with deposition temperature and deposition voltage and showed a linear relationship with depositon time. The relationships between the deposit yield and the parameters of electrophoretic deposition process were disscussed theoretically. SEM results indicate that the HA coatings on HA/Ti02 composite substrates prepared by two step electrophoretic deposition processes are even dense and uniform.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第13565287位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: wjqkbm@163.com

渝公网安备 50010702501715号