李召伟,何明奕,王胜民,魏源.机械镀Zn-Ti复合镀层的性能[J].表面技术,2008,37(6):54-56.
LI Zhao-wei,HE Ming-yi,WANG Sheng-min,WEI Yuan.Performance of Mechanical Zn-Ti Plating[J].Surface Technology,2008,37(6):54-56
机械镀Zn-Ti复合镀层的性能
Performance of Mechanical Zn-Ti Plating
投稿时间:2008-08-25  修订日期:2008-12-10
DOI:
中文关键词:  机械镀  Zn-Ti复合镀层  耐腐蚀性
英文关键词:Mechanical plating  Zn-Ti coating  Corrosion resistance
基金项目:国家自然科学基金资助项目(50561003)
作者单位
李召伟 昆明理工大学材料保护研究所,云南昆明650093 
何明奕 昆明理工大学材料保护研究所,云南昆明650093 
王胜民 昆明理工大学材料保护研究所,云南昆明650093 
魏源 昆明理工大学材料保护研究所,云南昆明650093 
AuthorInstitution
LI Zhao-wei Material Prorection Institute, Kunming University of Science and Technology, Kunming 650093, China 
HE Ming-yi Material Prorection Institute, Kunming University of Science and Technology, Kunming 650093, China 
WANG Sheng-min Material Prorection Institute, Kunming University of Science and Technology, Kunming 650093, China 
WEI Yuan Material Prorection Institute, Kunming University of Science and Technology, Kunming 650093, China 
摘要点击次数:
全文下载次数:
中文摘要:
      在机械镀锌中添加钛盐,获得了Zn-Ti复合镀层,使得镀层具有比纯锌镀层更加优良的耐蚀性能。试验中利用体视显微镜、扫描电子显微镜观察分析了机械镀Zn-Ti复合镀层的表面形貌和断口结构,对其孔隙率、结合强度、耐腐蚀性等性能进行检测,并分析添加钛盐对镀层性能的影响。结果表明:机械镀Zn-Ti复合镀层是一种综合性能优良的防护镀层,比机械镀纯锌层外观更为均匀光滑,无贯穿性孔隙,结合力和耐腐蚀性均优于机械镀锌层。
英文摘要:
      The Zn-Ti composite coating was prepared by adding of Ti in mechanical plating. The coating has more good corrosion resistance than pure Ti coating. Surface morphology and structure of fracture surface of mechanical Zn-Ti plating were studied using stereomicroscopy and scanning electronic microscopy. The porosity, bonding strength and corrosion resistance were detected and the influence of adding Al on its cladding performance was analyzed. The result shows that mechanical Zn-Ti plating is a kind of protection film with fine integral performance, smoother than mechanical galvanizing layer, without porosity, with high impact resistance and it' s corrosion resistance is better than that of galvanizing layer.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第14440123位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: wjqkbm@163.com

渝公网安备 50010702501715号