轧辊表面残余应力测试方法的对比试验研究
Contrast Experimental Study on Residual Stress Measurement of Roller
投稿时间:2008-08-18  修订日期:2008-12-10
DOI:
中文关键词:  残余应力  轧辊  检测方法  临界纵波
英文关键词:Residual stress  Roller  Test method  Critical refracted longitudinal wave
基金项目:浙江省自然科学基金( Y106187)
作者单位
虞付进 浙江师范大学机械装备与测控技术研究所,浙江金华321004 
华云松 上海理工大学,上海200093 
张克华 1.浙江师范大学机械装备与测控技术研究所,浙江金华321004;2.浙江工业大学,浙江杭州310032 
丁金福 浙江师范大学机械装备与测控技术研究所,浙江金华321004 
AuthorInstitution
YU Fu-jin Institute of Machinery Equipment and Measurement & Control Technology, Zhejiang Normal University, Jinhua 321004, China 
HUA Yun-song University of Shanghai for Science and Technology, Shanghai 200093, China 
ZHANG Ke_hua 1. Institute of Machinery Equipment and Measurement & Control Technology, Zhejiang Normal University, Jinhua 321004, China;2. Zhejiang University of Technology, Hangzhou 310032, China 
DING Jin-fu Institute of Machinery Equipment and Measurement & Control Technology, Zhejiang Normal University, Jinhua 321004, China 
摘要点击次数:
全文下载次数:
中文摘要:
      轧辊体积大且辊面状态又不好,尤其是热轧辊的表面常有氧化膜和微裂纹,在测量时又不能损伤轧辊表面,因此,轧辊残余应力的测量较困难。为验证临界折射纵波法测轧辊表面残余应力的准确性,用超声波法、X射线法和盲孔法对同一试件进行了应力测量。对这3种测量方法所测得的结果进行比较后,评价超声波法的可靠性和有效性。试验结果显示:临界折射纵波法测试的应力值与X射线衍射法和盲孔法测试的结果具有较好的一致性。
英文摘要:
      The residual stress measurement of roller is very difficult because that the roller has gigantic volume, the surface is out of order and especially there are oxide film and microcrack. In order to test the veracity of the method of the critical refracted longitudinal wave measurement (CRLWM) , the CRLWM method, the X radial method and the dead hole method were employed to test the residual stress, and the test result of this three methods was compared to evaluate reliability and validity of CRLWM. The result shows that the result of all of the test method is consentaneous.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第13565390位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: wjqkbm@163.com

渝公网安备 50010702501715号