李同道,王勇,韩彬.高铬铸钢激光熔凝组织与性能研究[J].表面技术,2008,37(1):40-41,74.
LI Tong-dao,WANG Yong,HAN Bin.Investigation on Laser Remelting and Property of High Chromium Cast Steel[J].Surface Technology,2008,37(1):40-41,74
高铬铸钢激光熔凝组织与性能研究
Investigation on Laser Remelting and Property of High Chromium Cast Steel
投稿时间:2007-08-23  修订日期:2008-02-10
DOI:
中文关键词:  高铬铸钢  激光熔凝  微观组织  硬度
英文关键词:High chromium cast steel  Laser remelting  Microstructure  Hardness
基金项目:山东省自然科学基金(Y2006F64)
作者单位
李同道 中国石油大学(华东)机电工程学院,山东东营257061 
王勇 中国石油大学(华东)机电工程学院,山东东营257061 
韩彬 中国石油大学(华东)机电工程学院,山东东营257061 
AuthorInstitution
LI Tong-dao School of Mechanical and Electronic Engineering of China University of Petroleum, Dongying 257061, China 
WANG Yong School of Mechanical and Electronic Engineering of China University of Petroleum, Dongying 257061, China 
HAN Bin School of Mechanical and Electronic Engineering of China University of Petroleum, Dongying 257061, China 
摘要点击次数:
全文下载次数:
中文摘要:
      为提高锅炉燃烧器喷嘴的表面性能,采用SkW横流C0:激光加工系统对高铬铸钢表面进行熔凝处理,并进行显微组织分析和硬度测试。研究结果表明:铸态高铬铸钢晶粒较粗大、组织不均匀,原始组织以奥氏体为基体,还存在大量网状断续共晶碳化物、莱氏体。经激光凝熔后,显微组织明显细化,其试样剖面组织分为激光熔凝区(细小奥氏体+少量细小未熔碳化物)、激光相变区(奥氏体+少量晶界碳化物)、过渡区和母材4个区域。熔凝区和相变硬化区的淬硬深度依工艺参数不同,可达0.2-0.3mm。由于形成了奥氏体组织,高铬铸钢表面硬度增加不明显,硬度最大值出现在相变硬化区。
英文摘要:
      In order to improve surface properties of the burning spraying nozzles of boilers , using a 5kW continuous wave C02 laser to perform the laser remelting treatment experiment on specimen of high chromium cast steel, the microstructure and the hardness of the specimen were measured. The results show that as cast structure of high chromium cast steel is coarsely and non-homogeneous, is mainly austenite, ledeburite and carbides. After laser remelting, the section is divided into remelted zone consisted of austenite and carbides, quenched zone composed of austenite and carbides, heat affected zone and base metal. The region and the hardness of various zones are related to the laser processing parameters. The hardening depth of melted zone and quenched zone may be up to Imm ~2mm. The hardening effect is not obvious after laser remelting treatment because the formation of austenite in remelting zone.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19497148位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号