宫晓静,许韵华,杨玉国,曹克宁,赵宇.高频脉冲电镀镍钴合金耐蚀性的研究[J].表面技术,2007,36(6):4-6.
GONG Xiao-jing,XU Yun-hua,YANG Yu-guo,CAO Ke-ning,ZHAO Yu.Corrosion Resistance of High Frequency Pulse Electroplating Ni-Co Coating[J].Surface Technology,2007,36(6):4-6
高频脉冲电镀镍钴合金耐蚀性的研究
Corrosion Resistance of High Frequency Pulse Electroplating Ni-Co Coating
投稿时间:2007-06-11  修订日期:2007-12-10
DOI:
中文关键词:  高频脉冲电镀  镍钴合金  复合镀层  耐蚀性
英文关键词:High frequency pulse electroforming  Ni-Co alloy  Composite coating  Corrosion resistance
基金项目:
作者单位
宫晓静 北京交通大学理学院化学所,北京100044 
许韵华 北京交通大学理学院化学所,北京100044 
杨玉国 北京交通大学理学院化学所,北京100044 
曹克宁 北京交通大学理学院化学所,北京100044 
赵宇 北京交通大学理学院化学所,北京100044 
AuthorInstitution
GONG Xiao-jing Institute of Chemistry, Science of School, Beijing Jiaotong University, Beijing 100044, China 
XU Yun-hua Institute of Chemistry, Science of School, Beijing Jiaotong University, Beijing 100044, China 
YANG Yu-guo Institute of Chemistry, Science of School, Beijing Jiaotong University, Beijing 100044, China 
CAO Ke-ning Institute of Chemistry, Science of School, Beijing Jiaotong University, Beijing 100044, China 
ZHAO Yu Institute of Chemistry, Science of School, Beijing Jiaotong University, Beijing 100044, China 
摘要点击次数:
全文下载次数:
中文摘要:
      用电化学的方法研究了高频脉冲电镀Ni-Co复合镀层在NaCI溶液中的耐蚀性,结果表明:随着频率的增加,沉积速率提高,沉积层表面更加致密、均匀,在3.5% NaCl溶液中Ni-Co镀层的腐蚀失重明显减小,腐蚀失重速率变慢;高频和直流电铸Ni-Co复合镀层的阳极极化曲线形状相似,随频率增加,自腐蚀电位正移,自腐蚀电流降低。可见,高频率对沉积层的细化有重要影响,并使镀层的耐蚀性提高。
英文摘要:
      The corrosion resistance of high frequency pulse electroforming Ni-Co coating in 3. 50-/o NaCl solution was studied. The results indicated that, as the frequency increased, the depositing rate got improved, the coating tended to be more compact and the weight loss rate of the film immersed in 3. 50-/o NaCl solution decreased. The anodic polarization curves for the platings electroformed at high frequency were similar to that for the platings electroformed at DC. As the frequency increased, Ecorr shifted in positive direction, /con decreased. Thus high frequency was of great impact on the deposited layers and improved the corrosion resistance of the plating.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19510303位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号