金刚石的嵌入对其复合镀层的影响分析
Discussions about Effects of Diamond Incorporation on the Microstructure of Electroplated Ni-Co-diamond Composites
投稿时间:2007-07-03  修订日期:2007-10-10
DOI:
中文关键词:  电沉积  复合镀层  Ni-Co-金刚石  显微结构  金刚石磁性
英文关键词:Electrodeposition  Composite deposite  Ni-Co-diamond  Microstructure  Metallic inclusion magnetization
基金项目:河南省自然科学基金项目(0411051300)。
作者单位
李云东 河南农业大学机电工程学院,河南郑州450002 
卢汇洋 河南农业大学机电工程学院,河南郑州450002 
苏宗伟 河南农业大学机电工程学院,河南郑州450002 
丁俊成 河南农业大学机电工程学院,河南郑州450002 
AuthorInstitution
LI Yun-dong College of Mechanical and Electrical Engineering, Henan Agricultural University, Zhengzhou 450002, China 
LU Hui-yang College of Mechanical and Electrical Engineering, Henan Agricultural University, Zhengzhou 450002, China 
SU Zong-wei College of Mechanical and Electrical Engineering, Henan Agricultural University, Zhengzhou 450002, China 
DING Jun-cheng College of Mechanical and Electrical Engineering, Henan Agricultural University, Zhengzhou 450002, China 
摘要点击次数:
全文下载次数:
中文摘要:
      金属一金刚石共沉积复合镀层,在不同应用领域(如提高耐磨性、自润滑性、切削性及弥散强化效果等)已得到广泛关注。详述了金刚石的嵌入对复合镀层的影响及其原因。试验发现,金刚石的嵌入恶化了复合镀层胎体的微观结构,使得胎体晶粒粗化、镀层和颗粒结合部出现间隙、镀层表面起伏不平并出现节瘤、沟谷及金刚石颗粒表面的过度包镶等现象。分析发现,以上现象是金刚石晶体内部金属包裹体的磁性,对运动的阳离子产生洛仑兹力作用,从而影响电沉积过程的结果。
英文摘要:
      Electrodeposited diamond composite coatings have been widely studied for improving the hardness, wear resistance and self-lubrication. The detrimental impacts of diamond incorporation on the composites microstructure was reported. It is shown that the incorporation significantly worsens the microstructure , like coarsening the matrix grain , inducing gaps between matrix and diamonds, and promoting emergence of domed nodules, valleys and over-plating cases on the fluctuant matrix surface. All the deterioration facts are believed to arise from metallic inclusions trapped in diamond crystals during their synthetic process.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19495819位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号