郑高,杜楠,梁红波.纳米二氧化钛表面改性及其在聚氨酯涂层中的分散性质[J].表面技术,2007,36(4):42-44,48.
ZHENG Gao,DU Nan,LIANG Hong-bo.The Surface Modification of Nano-Ti02 and Its Distribution in Polyurethane Coatings[J].Surface Technology,2007,36(4):42-44,48
纳米二氧化钛表面改性及其在聚氨酯涂层中的分散性质
The Surface Modification of Nano-Ti02 and Its Distribution in Polyurethane Coatings
投稿时间:2007-03-29  修订日期:2007-08-10
DOI:
中文关键词:  纳米Ti0.  表面改性  纳米复合涂层  分散性  聚氨酯涂层
英文关键词:Nano-Ti02  Surface modification  Nano-composite coatings  Distribution  Polyurethane coating
基金项目:
作者单位
郑高 南昌航空工业学院,江西南昌330063 
杜楠 南昌航空工业学院,江西南昌330063 
梁红波 南昌航空工业学院,江西南昌330063 
AuthorInstitution
ZHENG Gao Nanchang Institute of Aeronautical Technology, Nanchang 330063 , China 
DU Nan Nanchang Institute of Aeronautical Technology, Nanchang 330063 , China 
LIANG Hong-bo Nanchang Institute of Aeronautical Technology, Nanchang 330063 , China 
摘要点击次数:
全文下载次数:
中文摘要:
      采用长链烷烃和微胶囊方法对纳米Ti0.(锐钛型,粒径20nm)进行表面改性,利用傅里叶红外光谱(FTIR)和热重分析(TCA)分别研究了改性纳米粉体的表面化学结构及接枝率,结果表明:改性纳米Ti0.粉体表面成功接枝了高分子聚合物,接枝率分别为5%和12%。将改性纳米Ti01粉体(质量分数为1% - 3%)与双组分聚氨酯涂料进行复合,制备了纳米Ti0:/聚氨酯复合涂料,并利用扫描电子显微镜(SEM)对纳米复合涂层进行了微观检测,结果表明:微胶囊改性的纳米Ti01在涂层中的分散性最好。
英文摘要:
      The surface of nano-Ti02 ( anatase , particle diameter 20nm) was modified by long-chain alkane or microcapsule, which was characterized by fourier tmsform infrared ray ( FTIR) and thermal analysis ( TGA) . The results show that the modified nano-Ti02 particles have been grafted by macromolecular polymers, with the grafting degrees of 50-/o and 120-/o , respectively. The modified nano-Ti02 ( 10-/o - 30-/o ) was blended with polyurethane resins to obtain nanoTi02/ polyurethane composite coating, which were further studied by scanning electron microscopy( SEM) . The results show that nano-Ti02 which was modified by microcapsule has the best dispersibility.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19499471位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号