赵辉,王群,丁彰雄,张云乾.HVOF喷涂纳米结构WC-12Co涂层的组织结构分析[J].表面技术,2007,36(4):1-3,14.
ZHAO Hui,WANG Qun,DING Zhang-xiong,ZHANG Yun-qian.Microstructural Analysis of Nanostructured WC-12Co Coatings Sprayed by HVOF[J].Surface Technology,2007,36(4):1-3,14
HVOF喷涂纳米结构WC-12Co涂层的组织结构分析
Microstructural Analysis of Nanostructured WC-12Co Coatings Sprayed by HVOF
投稿时间:2007-02-13  修订日期:2007-08-10
DOI:
中文关键词:  HVOF  纳米结构涂层  陶瓷涂层  WC-12Co  组织结构
英文关键词:HVOF  Nanostructured coatings  Ceramic coating  WC-12Co  Microstructure
基金项目:国家自然科学基金资助项目(50479016)
作者单位
赵辉 武汉理工大学能源与动力工程学院,湖北武汉430063 
王群 湖南大学材料科学与工程学院,湖南长沙410082 
丁彰雄 武汉理工大学能源与动力工程学院,湖北武汉430063 
张云乾 武汉理工大学能源与动力工程学院,湖北武汉430063 
AuthorInstitution
ZHAO Hui College of Energy & Power Engineering, WUT, Wuhan 430063,China 
WANG Qun Materials Science & Engineering College, Hunan University, Changsha 410082,China 
DING Zhang-xiong College of Energy & Power Engineering, WUT, Wuhan 430063,China 
ZHANG Yun-qian College of Energy & Power Engineering, WUT, Wuhan 430063,China 
摘要点击次数:
全文下载次数:
中文摘要:
      纳米结构WC-12Co涂层的研究目前已受到了广泛重视,对其组织结构及影响因素的研究有利于提高涂层性能。采用HVOF工艺制备了纳米结构、多峰结构及普通微米结构3种WC-12Co金属陶瓷复合涂层,并采用SEM、XRD等对粉末及涂层的显微形貌、组织结构进行了分析;探讨了粉末在喷涂过程中的氧化脱碳机理,并指出了与之相关的影响因素。结果表明:纳米结构WC-12Co涂层结构致密,孔隙率低,与基体结合状态良好;纳米粉末在喷涂过程中比微米粉末氧化失碳严重,并发生了不同的纳米晶粒的长大;纳米粉末在喷涂过程中的氧化脱碳程度不仅与喷涂工艺有关,还在很大程度上取决于粉末本身的结构特性。
英文摘要:
      Research on nanostructured WC-12Co coatings has been emphasized nowadays, and study on coating s microstructure and the influencing factors is beneficial to enhance the coating properties. Nanostructured, multimodal and conventional WC-12Co ceramic coatings were deposited by high velocity oxy-fuel spray ( HVOF) and the structures of the coatings such as microstructures and phase compositions were analyzed by SEM and XRD. Finally the mechanisms and factors of decarburization of WC particles in spraying were explored. Research results show that microstructures of nanostructural and multimodal WC-12Co coatings deposited by HVOF are dense, better adhesive strength and little porosity than conventional one. As well, it is found that although obvious decarburization of WC and crystal size growth occurred during spraying multimodal and nanostructured WC-12Co powders in comparison with conventional coating, the decarburization of WC for the nanostructured powder is more severe because of the increasement in nano size WC amount , and the decarburization degree of nanostructured WC-Co is not only influenced by spray parameters , but also depended on the powder structure characteristics.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第13583893位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: wjqkbm@163.com

渝公网安备 50010702501715号