刘文科,曹小华,彭述明,龙兴贵,杨本福,罗顺忠,王维笃.钛膜表面阳极氧化层制备及表征[J].表面技术,2007,36(1):51-55.
LIU Wen-ke,CAO Xiao-hua,PENG Shu-ming,LONG Xing-gui,YANG Ben-fu,LUO Shun-zhong,WANG Wei-du.Preparation of Anode Oxidation Layer on the Surface of Titanium Film and its Surface Property[J].Surface Technology,2007,36(1):51-55
钛膜表面阳极氧化层制备及表征
Preparation of Anode Oxidation Layer on the Surface of Titanium Film and its Surface Property
投稿时间:2006-09-11  修订日期:2007-02-10
DOI:
中文关键词:  钛膜,阳极氧化,制备,表征
英文关键词:Titanium film  Anode oxidation  Preparation  Surface property
基金项目:中国工程物理研究院行业预研基金(20020536)和中国工程物理研究院核物理与化学研究所科技创新基金(805)资助
作者单位
刘文科 中国工程物理研究院 四川绵阳 621900 
曹小华 中国工程物理研究院 四川绵阳 621900 
彭述明 中国工程物理研究院 四川绵阳 621900 
龙兴贵 中国工程物理研究院 四川绵阳 621900 
杨本福 中国工程物理研究院 四川绵阳 621900 
罗顺忠 中国工程物理研究院 四川绵阳 621900 
王维笃 中国工程物理研究院 四川绵阳 621900 
AuthorInstitution
LIU Wen-ke Institute of Nuclear Physics and Chemistry, China Academy of Engineering Physics, Mianyang 621900, China 
CAO Xiao-hua Institute of Nuclear Physics and Chemistry, China Academy of Engineering Physics, Mianyang 621900, China 
PENG Shu-ming Institute of Nuclear Physics and Chemistry, China Academy of Engineering Physics, Mianyang 621900, China 
LONG Xing-gui Institute of Nuclear Physics and Chemistry, China Academy of Engineering Physics, Mianyang 621900, China 
YANG Ben-fu Institute of Nuclear Physics and Chemistry, China Academy of Engineering Physics, Mianyang 621900, China 
LUO Shun-zhong Institute of Nuclear Physics and Chemistry, China Academy of Engineering Physics, Mianyang 621900, China 
WANG Wei-du Institute of Nuclear Physics and Chemistry, China Academy of Engineering Physics, Mianyang 621900, China 
摘要点击次数:
全文下载次数:
中文摘要:
      为了研究钛膜表面阳极氧化层对吸附和解吸氢同位素特性的影响,需制备和表征钛膜表面阳极氧化层。本文设计了钛膜表面阳极氧化装置,确定了制备厚度不同的氧化层的阳极氧化工艺参数,其工艺简单、易操作;并对阳极氧化层进行了AES深度剖析和XPS化合价分析。其结果如下:在确定的工艺参数下,设计加工的阳极氧化装置能够制备出表面呈彩色的阳极氧化层,而且表面平整、光滑、均匀,与基体金属结合牢固;采用AES深度剖析确定了阳极氧化层的厚度,而且在其它条件相同时,获得阳极氧化层的厚度随着电压、H2SO4浓度和时间的增加而明显变厚的规律;采用XPS研究了阳极氧化层钛的主要价态为+4、+3和+2价,氧化层主要组成为TiO2、Ti2O3和TiO。
英文摘要:
      It was necessary that anode oxidation layers are prepared on the surface of titanium film and its surface property is ascertained for the sake of investigating effects of anodic oxide layers on characteristics of absorbing and desorbing hydrogen isotope. Anodic oxidation apparatus on the surface of titanium film of molybdenum substrate is designed. The technical parameters of anodic oxidation what determine the thickness of anode oxidation layers are ascertained. The AES profile and XPS valency analysis of anode oxidation layer are measured. The results indicate that the color anode oxidation layers are prepared by using anodic oxidation apparatus designed and machined in the ascertained technical parameters of anodic oxidation, the oxidation technique is simple, and operated easily. The surface of the anode oxidation layers is flat, slick and uniform, and the anode oxidation layers link firmly with titanium films. The anode oxidation layers thicken with the increasing of voltage, concentration of H2SO4 and time respectively when other condition is uniform. Titanium valency on the surface of oxide layers is analyzed by XPS, and its result shows that titanium valency mainly is +4, +3 and +2 .The component is TiO2, Ti2O3 and TiO mainly in the anode oxidation layers.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19850045位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号