尹磊,冯圣玉,吴苏友,赵云鹏.耐候防腐涂层的动态力学行为研究[J].表面技术,2007,36(1):25-27.
YIN Lei,FENG Sheng-yu,WU Su-you,ZHAO Yun-peng.Dynamic Mechanical Analysis of Durable And Anticorrosive Coatings[J].Surface Technology,2007,36(1):25-27
耐候防腐涂层的动态力学行为研究
Dynamic Mechanical Analysis of Durable And Anticorrosive Coatings
投稿时间:2006-10-03  修订日期:2007-02-10
DOI:
中文关键词:  防腐涂层  动态力学性能  聚氨酯涂料  环氧树脂涂料
英文关键词:anticorrosive coating  DMA  polyurethane coating  epoxy coating
基金项目:
作者单位
尹磊 1.山东大学化学与化工学院,济南 250010;2.中国兵器工业集团第五三研究所,济南 250031 
冯圣玉 山东大学化学与化工学院,济南 250010 
吴苏友 中国兵器工业集团第五三研究所,济南 250031 
赵云鹏 中国兵器工业集团第五三研究所,济南 250031 
AuthorInstitution
YIN Lei 1.College of Chemistry and Chemical Engineering,Shan Dong University,Jinan 250010, China;2.Institute 53 of China’s Ordnance Industry Group, Jinan 250031, China 
FENG Sheng-yu College of Chemistry and Chemical Engineering,Shan Dong University,Jinan 250010, China 
WU Su-you Institute 53 of China’s Ordnance Industry Group, Jinan 250031, China 
ZHAO Yun-peng Institute 53 of China’s Ordnance Industry Group, Jinan 250031, China 
摘要点击次数:
全文下载次数:
中文摘要:
      为了考察耐候防腐涂层在承受应力时性能的变化情况,采用DMA(动态力学分析)方法评价了几种耐候防腐涂料的动态力学性能,研究了贮存模量、消耗模量和tanδ三个动态参数和温度之间的关系。揭示了几种涂料体系的结构与组成对涂膜的力学性能和耐化学试剂性能的影响。分析结果表明,采用DMA方法可以分析比较耐候防腐涂料的不同性能特征:具有均一交联的涂膜的聚氨酯涂料和环氧涂料能提供较好的耐化学介质性,具有不均一交联涂膜的聚氨酯涂料具有较好的低温柔韧性。此项研究可为防腐涂料在车辆上的合理应用提供理论依据。
英文摘要:
      Several durable and anticorrosive coatings were evaluated using DMA in order to investingate the properties variation of these coatings during the stress. The relationship between modulus and temperature as well as tanδ-T were studied. DMA investigations revealed that structures and formation had a great influence on the mechanical properties and the chemical agent resistance of coatings. The results indicate that different characteristic properties can be compared to using DMA: the more uniformly cross-linked polyurethane coating and epoxy coating provided the best chemical agent resistance, the poor uniformly cross-linked polyurethane coating provided the best mechanical properties.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19990933位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号